Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 108 MPa | 15700 psi | 50 mm/min; ASTM D638 |
Ovation Polymers RIGITRON 30530 GF Polyester, 30% Glass Reinforced Polyester – 30 % Glass Fiber Reinforced PET. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM standards. Va.. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 1200 A 13 Black 13 Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | 10mm/min; ASTM D638 |
Kingfa JH-R0G30 Flame Retardant and 30% Glass Fiber Reinforced PC/ABS Alloy Features:UL V-0 @ 3.2mmExcellent balance propertiesHigh stiffnessGood size stabilityGood processing propertiesApplications:Injection moldingAutomobile instrument panelCD-ROM base pick-upOA device an.. |
|||
Tensile Strength at Break | 108 MPa @Thickness 3.20 mm |
15700 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical Lupox® GP2306FY PBT+GF30% Description: Injection Molding, PBT+GF30%Flame Retardant, GWITApplication: IT/OA, E&E (Connector)CAS No. 88497-56-7, 65997-17-3, 37640-57-6, 24968-12-5, 25038-59-9 and 1309-64-4Information provided .. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PX5558 PPE+PS 30% glass reinforced, high flow PPO. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp OFP36A PPS - Branched LNP LUBRICOMP* OFP36A is a compound based on PPS - Branched resin containing Glass Fiber, Silicone, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SA.. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp OFP36A PPS - Branched (Asia Pacific) LNP LUBRICOMP* OFP36A is a compound based on PPS - Branched resin containing Silicone, PTFE, Glass Fiber. Added features of this material include: Internally Lubricated.This data was supplied by SA.. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® ENH4560 PBT (Asia Pacific) Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ4860HR PBT Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ4860HR PBT (Asia Pacific) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® IQNH4560 PBT (Asia Pacific) Valox* IQNH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC LNP* Thermocomp* DF0049P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DF005 PC LNP* Thermocomp* DF005 is a compound based on Polycarbonate containing 25% Glass Fiber. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp GF008 PSU LNP* Thermocomp* GF008 is a compound based on Polysulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp GF008 PSU (Europe-Africa-Middle East) LNP* Thermocomp* GF008 is a compound based on Polysulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HF-3200H PC, Glass Filled High Impact Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HF-3200H PC, Glass Filled High Impact Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DE003ER PC (Asia Pacific) LNP STAT-KON* DE003ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP BF004 SAN LNP* THERMOCOMP* BF004 is a compound based on SAN resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC (Asia Pacific) LNP* Thermocomp* DF0049P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ISO 527 |
SABIC Innovative Plastics LNP Thermocomp SF006S PA 12 LNP* Thermocomp* SF006S is a compound based on Nylon 12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas re.. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ISO 527-1 |
Vyncolit Vyntec® CF8131 Carbon Fiber Reinforced Phenolic VYNTEC CF8050 is a carbon fiber reinforced phenolic moldable composite with good tribological and superior mechanical properties combined with low density. Very good chemical resistance in several o.. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® LW9020 BK580 PBT+ASA
(Unverified Data**) 20% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9020 BK580 is a 20% glass fiber reinforced black polybutylene terephthalate blend for injection mol.. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 80G33HS1L NC010 Nylon 66
(Unverified Data**) 33% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G33HS1L NC010 is a 33% glass fiber reinforced heat stabilized polyamide 66 resin with outstanding impact resistance developed usin.. |
|||
Tensile Strength at Break | 108 MPa | 15700 psi | ISO 527 |
Azdel Plus R401-B01 40% Continuous Random Fiber Mat / PP Resin Matrix AZDEL® R401-B01 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a polypropylene resin matrix. This composite material features high flow pr.. |