Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 110 MPa | 16000 psi | |
Plastcom SLOVAMID 66 GF 13 TS PA66, 13% glass fibre FeaturesChemically reinforced with 13% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. W.. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
Lanxess Pocan® KL 1-7265 000000 PBT, 15% Glass Fiber PBT, 15% glass fibers, injection molding |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND G3240U PP SABIC® PPcompound G3240U is a general purpose, 40% glass filled, chemically coupled, heat stabilized and UV stabilized homopolymer polypropylene compound. The IMDS ID is 209768078. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527 Type 1A |
Solvay TECHNYLSTARâ„¢ S 218 MZ20 V10 Black 2N PA6, 20% mineral, 10% glass filled, DRY Description: TECHNYL STAR Polyamide, 20% mineral filled and 10% of glass fiber reinforced, heat stabilized, for injection molding. Characterized by a high fluidity of the melt.Available in: Europe a.. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 4521 PBT (Europe-Africa-Middle East) VALOX 4521 is a high flow, 19.5% glass reinforced flame retardant PBT injection moulding resin. Applications: electrical applications. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 508R PBT+PC 30% GR PBT+PC. Excellent mechanical and thermal performance. Non-FR. Reduced warpage characteristics. Applications same as VALOX 420R. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xylex X8419 PC+POLYESTER Low-medium flow, suitable for blow molding, injection molding, extrusion.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 508 PBT+PC (Asia Pacific) 30% GR PBT+PC. Excellent mechanical and thermal performance. Non-flame retardant. Reduced warpage characteristics. Applications same as VALOX 420. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
DSM Akulon® K224-G6 (Cond.) 30% Glass Reinforced Nylon 6 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
DSM Akulon® K224-G6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Cond) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
DSM Arnite® TV4 240 S PBT-20% Glass Reinforced (European and Asian Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 5052 (BGZ-15 FC) PA6-GF15 Product description: Grilon XE 5052 is a impact modified, heat stabilized PA 6 injection molding grade with 15% glass fiber: High impact resistanceGood surface qualityShort cycle timeGood flowabilit.. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 73G30HSL BK261 Nylon 6
(Unverified Data**) 30% Glass Reinforced Heat Stabilized Polyamide 6 Zytel 73G30HSL BK261 is a 30% glass fiber reinforced heat stabilized lubricated black polyamide 6 for injection molding. It has excellent surface app.. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 73G30T BK261 Nylon 6
(Unverified Data**) 30% Glass Reinforced Toughened Polyamide 6 Zytel 73G30T BK261 is a 30% glass fiber reinforced toughened black polyamide 6 resin for injection molding.Information provided by DuPont Performance Polym.. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
DSM Akulon® Ultraflow™ K-FG6 Nylon 6-30% Glass Reinforced (European Grade) (Cond) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
Beijing Chemical Industry KAIFA® 302-G30 PBT Resin 30% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | 50mm/min; ISO 527 |
Teijin Panlite® BS-8110R Friction and Abrasion Resistant, Carbon Fiber Reinforced Polycarbonate Resin CF 10% reinforced grade, meeting UL 94 V-2. it is compounded with fluorine powder to improve friction and abrasion resistance and also exhibits a mold release property, maintaining excellent charact.. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 3412R PC 20% GR, provides improved mechanical properties and UL94 V-1 rated at 0.058"". Internal mold release added. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
Beijing Chemical Industry KAIFA® MN301-G20 Nylon 66 Resin 20% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® BKV 35 H2.0 901510 Nylon 6, 35% Glass Fiber PA 6, injection molding grade, 35% glass fibers, good heat-ageing resistanceApplication Examples: automotive structures |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
Mitsui Arlen™ C215 15% Glass Fiber-Reinforced Modified Nylon 6T (DAM) ARLEN™ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320°C) and a rigidity level comparable to super engineering plastics, it possesses .. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 80G14AHS BK099 Nylon 66
(Unverified Data**) 14% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G14AHS BK099 is a 14% glass fiber reinforced toughened high flow heat stabilized black polyamide 66 resin. It offers outstanding p.. |
|||
Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
Oxford Polymers 20GF 20% Glass Fiber Filled Polycarbonate for Injection Molding 20% Glass Fiber Filled Polycarbonate for Injection MoldingInformation provided by Oxford Polymers. |