Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 13.1 MPa | 1900 psi | Flow; DIN 53504 |
PolyOne OnFlex™ U 5365A-E0134 FG Thermoplastic Elastomer (TPE) OnFlex™ U 5365A-E0134 FG is a performance TPU alloy designed for use in injection molding application where FDA compliance and Overmolding onto PC, ABS and PC/ABS substrates are required.Properties.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne FireCon™ CPE 0883-01 RoHS BLACK Polyethylene, Chlorinated (CPE) CPE-0833-1 RoHS BLACK is a heavy duty thermoplastic jacket for power and control cables. It is suitable for VW1 and tray fire rated applications. CPE-0833-1 RoHS BLACK offers the highest level of fi.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B7501 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible C8500 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R5165A Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D4745 |
3M Dyneon™ CC607 Custom Fluoropolymer Compound
(discontinued **) This compound consists of a mixture of 35% fiberglass blended with PTFE.Information provided by Dyneon, A 3M Company |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
LyondellBasell Plexar® PX2250 Extrudable Tie-Layer Resin, Anhydride Modified HDPE Plexar® tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, s.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | |
Indium Corp. Indalloy 128 Pure Tin Information Provided by Indium Corporation |
|||
Tensile Strength at Break | >= 13.1 MPa | >= 1900 psi | ASTM D412 Method A |
Seals Eastern 7204 Ethylene-Propylene Rubber Y267-Type EPDM for geothermal steam service. Ultra-Low compression set.Information provided by Seals Eastern, Inc. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
Teknor Apex APEX® 154 Polyvinyl Chloride, Flexible Notes: 80°C Jacket; RoHS Compliant Uses: Military Cable Jacketing; Non-flexible JacketingForms: Pellets Wire Types: Molded Components Agency Ratings: MIL C-915-C Additional Information: Temperatu.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
Teknor Apex APEX® 3601-65 Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Agency Ratings: NSF 61 Forms: Pellets Additional Information: Second Generation SeriesInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
Teknor Apex APEX® 4109 Polyvinyl Chloride, Flexible Notes: 60°C General Purpose; RoHS Compliant Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molde.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D412 |
Teknor Apex Monprene® MP-1688A Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
Teknor Apex APEX® 07-U0296A-65 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
Teknor Apex APEX® 90-R471U-70-NT Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D412 |
Teknor Apex Monprene® MP-2990 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D412 |
Teknor Apex Telcar® TL-8712R Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D412 |
Borealis PC0787 Polyethylene Insulation Compound, Crosslinkable PC0787 is a flame retardant crosslinking polyethylene compound for low voltage insulation. PC0787 contains flame retardant additives to reduce normal flame spread characteristics so as to achieve a.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EC4041AA Low Density Polyethylene WESTLAKE low-density polyethylene EC4041 is recommended for use in the boardstock coating industry. The resin has low neck-in and good drawdown characteristics. Coatings produced from EC4041 have ex.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
ExxonMobil LLDPE LL 1004YB Wire & Cable Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1004YB is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. The grade contains a higher l.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
ExxonMobil LLDPE LL 5002.09 Linear Low Density Polyethylene Resin Product Description: LL 5002.09 is a linear low density polyethylene resin designed to provide good processability and ease of blending. LL 5002.09 also exhibits good toughness and environmental str.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | |
3M Scotch-Weld™ DP8010 Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polypropyl.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | cured; ISO 6922 |
3M Scotch-Weld™ LO5 Low Odor Instant Adhesive 3M™ Scotch-Weld™ Low-Odor Instant Adhesives are formulated to have low volatility while maintaining bonding of a wide rage of materials. Low volatility means that these products are not only low o.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | cured, grit-blasted steel; ASTM D2095 |
3M Scotch-Weld™ MG05 LO Medical Grade Instant Adhesive 3M™ Scotch-Weld™ Medical Grade Instant Adhesive are intended for use on a wide variety of materials used in the construction of disposable medical assemblies. They will quickly bond metals, plasti.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | |
3M SMS Heat Shrink Tubing 3M Heat Shrink Tubing SMS is a co-extruded, dual wall product. It is a composite of a polyolefin shrinkable outer wall and a thermoplastic adhesive inner wall. SMS tubing does not degrade when expos.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | |
Abatron AboCast/AboCure 8007-2 High-Grade Polysulfide-Epoxy Flexible Membrane Sealant and Joint-Filler AboCast/AboCure 8007-2 is a 2-part polysulfide-epoxy solventless system. It is weather- and water-proof, flexible, and acid, alkali, and fuel resistant. Uses: Filling joints and cracks in exposed s.. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | |
3M EPS-400 Heat Shrink Tubing 3M Heat Shrink tubing EPS-400 is a medium-wall, semi-rigid tubing offering the advantages of integral, adhesive-lined construction. The tubing is made from flame-retardant, flexible polyolefin with .. |
|||
Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
Teknor Apex APEX® 90-A471R-70-NT Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Radiation (Gamma) Resistant; Radiation Sterilizable Uses: Medical/Healthcare Applications; Tubing Processing Method: Extrusion Forms: PelletsInformation Provided by Tekno.. |