Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 130 MPa | 18900 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID 66 GF 30 FRA 3 Polyamide 66, 30% Glass Fiber, Halogen Flame Retardant FeaturesPA 66 for injection moulding, reinforced with 30% glass fiber and halogen flame retardant. Application in electrical industry: breakers, coil forms, covers, terminals. Slightly decreased f.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 37 |
Polyplastic Armamid® PA GF25-1FR Nylon 6, 25% Glass Fiber Flame retardant, RoHS compliantInformation provided by PolyPlastic Group. |
|||
Tensile Strength at Break | <= 130 MPa | <= 18900 psi | ISO/R527 |
Polykemi AB SCANAMID 66 A13^ F15 Nylon 66, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | 10mm/min; ASTM D638 |
Kingfa PA66-G15 15% Glass Fiber Reinforced PA66 Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
Lanxess Durethan® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, higher impact and notched impact strength and also higher energy absorption under biaxial impact load than BKV 130, conditioning .. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1,-2 |
Lanxess Durethan® BKV 325 Z H2.0 901510 Nylon 6, 25% Glass Fibers PA 6, 25% glass fibers, blow molding, impact modified, heat-ageing stabilized |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DE003Z PC LNP STAT-KON* DE003Z is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Extrusion Grade. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON RE004MPC PA 66 LNP* STAT-KON* RE004MPC is a compound based on Nylon 66 resin containing 20% Milled Carbon Fiber. Added features of this material are: Exceptional Processing, Clean Compound System, Electrically C.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DF0089 PC LNP THERMOCOMP* DF0089 is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features include: Flame Retardant. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Akulon® K224-G4U (Dry) 23% Glass Reinforced Nylon 6 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® BG-40 HM PA6-GF40 Product description: Grilon BG-40 HM is a heat stabilized, normal viscosity, and adhesion modified PA6 injection molding grade with 40% glass fibers. Grilon BG-40 HM has the following important prop.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6600/50 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-35 PA666-GF35 Information provided by EMS Grivory |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-35/4 H black 9836 PA666-GF35 Product description: Grilon TSG-35/4 H is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 35% glass fibers, modified for parts with high thermal demands. Grilon TSG-.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-35/4 PA666-GF35 Product description: Grilon TSG-35/4 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 35% glass fibers. Grilon TSG-35/4 has the following important properties: Good flo.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® HR5330HFS NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**) 30% Glass Reinforced Polybutylene Terephthalate with Improved Processing Crastin HR5330HFS is a 30% glass fiber reinforced moderately toughened hydrolysis resistant polybutylene terephthalate for in.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® SC193 NC010 PBT+SAN
(Unverified Data**) 30% Glass Reinforced Polybutylene Terephthalate Blend Developed for the Healthcare IndustryCrastin® SC193 is a 30% glass fiber reinforced polybutylene terephthalate blend for injection molding. It.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Minlon® 22C NC010 Nylon 66
(Unverified Data**) 38% Mineral/Glass Reinforced Polyamide 66 Minlon 22C NC010 is a 38% mineral/glass reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance Polym.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® HTN 54G15HSLR NC010 Polyphthalamide (PPA)
(Unverified Data**) 15% Glass Reinforced Toughened PPA High Performance Polyamide Zytel HTN54G15HSLR NC010 is a 15% glass reinforced toughened heat stabilized hydrolysis resistant high performance polyamide resin. It i.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® LBV-30H FWA nat PA12-GF30 Product Description: Grilamid LBV-30H FWA natural is a 30% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: Stiffness combined with h.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | 0.2 in/min; ASTM Test |
BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid 8267G HS BK-102 is a heat stabilized, black pigmented, 40% mineral and glass fiber reinforced nylon 6 injection molding compound. It possesses a balance of engineering properties in combin.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO R 527 |
Addiplast Addinyl C2 V15 Nylon 66/6, 15% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | ASTM D638 |
Solvay Specialty Polymers Veradel® AG-330 Polyethersulfone (PESU)
(Unverified Data**) Veradel AG-330 is a 30% glass fiber reinforced grade of polyethersulfone (PESU). Adding glass fiber to polyethersulfone substantially increases the rigidity, tensile strength, creep resistance, dime.. |
|||
Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® VX4029 PBT (Europe-Africa-Middle East) VALOX VX4029 is a 30% glass reinforced PBT injection moulding resin with excellent strength, stiffness, dimensional stability and high heat resistance. This grade is a 420 with reduced additive load.. |