Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Tensile Strength at Break = 13900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM VH1003F PEI Copolymer
Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant..
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM VH1003M PEI Copolymer (Asia Pacific)
Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Internal mold release. This product has thinwall FR capability and has a UL94 V0 listing. This mate..
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM VH1003M PEI Copolymer (Europe-Africa-Middle East)
Transparent, Thermoplastic Polyimide (TPI) resin. Glass transition Temp. (Tg) of 247°C. Internal mold release. This resin has thinwall FR capability and has a UL94 V0 listing. Resin is halogen free..
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM VH1003P PEI Copolymer (Asia Pacific)
Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Powder version of VH1003. This resin is a Dual-use item and is subject to export control restrictio..
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM XH1005 TPI Resin
Thermoplastic Polyimide Extem* XH1005 Resin.
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Europe-Africa-Middle East)
Thermoplastic Polyimide Extem* XH1005 Resin.
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM XH1015 TPI Resin
Thermoplastic Polyimide Extem* XH1015 Resin.
Tensile Strength at Break 96.0 MPa
13900 psi
50 mm/min; ASTM D638
Qualchem Danaprop PP1GF-30 Polypropylene, 30% Glass Fiber
Polypropylene (co-polymer) reinforced with glass fiberInformation provided by Qualchem Zrt.
Tensile Strength at Break 96.1 MPa

@Thickness 3.20 mm
13900 psi

@Thickness 0.126 in
50mm/min; ASTM D638
LG Chemical Lupox® LW5402A PBT+PC+GF40%
Description: Injection Molding, PBT+PC+GF40%, Low Warpage, High GlossApplication: E&E, Automotive (Bobbin, Switch)CAS No. 9010-86-0, 65997-17-3, 24968-12-5 and 103598-77-2Information provided by LG ..
Tensile Strength at Break 96.0 MPa
13900 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp EFP36G PEI
LNP* EFP36G is a Polyetherimide base resin containing a Mixed Glass Fiber and PTFE/Silicone.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 96.0 MPa
13900 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 (Asia Pacific)
LNP* Lubricomp* RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
Tensile Strength at Break 96.0 MPa
13900 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT (Europe-Africa-Middle East)
LNP* LUBRICOMP* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features include: Flame Retardant, Internally Lubricated.
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP ZFL24 PPE+PS
LNP* LUBRICOMP* ZFL24 is a compound based on PPE+PS resin containing 20% Glass Fiber, 10% PTFE. Added feature of this grade is: Wear Resistant.
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Lubricomp ZFL34 PPO
LNP* Lubricomp* ZFL34 is a compound based on Modified PPO containing glass fiber and PTFE.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem AUT230M PEI
Transparent polyetherimide (Tg 247 degC). Contains low level of mold release. Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are ..
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON Cycoloy_JK800 PC+ABS
LNP* Stat-kon* Cycoloy_JK800 compound is an 8% carbon fiber reinforcedPC+ABS, electrostatic dissipative ECO conforming FR. Good hydrolytic stability.
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem UR9076LG PEI
Standard flow mineral filled Polyetherimide Blend. Restricted sales to GE Specialty Film & Sheet.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM XH6050 PEI Copolymer
Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming, UL94 V0 listing. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM XH6050 PEI Copolymer (Asia Pacific)
Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming, UL94 V0 listing. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
Tensile Strength at Break 96.0 MPa
13900 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON DEL33EC PC
LNP STAT-KON* DEL33EC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 15% PTFE. Added features include: Clean Compounding System, Electrically Conductive, Wear Resistant, Ea..
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Valox® K4560 PBT (Europe-Africa-Middle East)
30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable.
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East)
DATA ON BK1005 ONLY.
Tensile Strength at Break 96.0 MPa
13900 psi
ASTM D 638
SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS
LNP STAT-KON* NX03602 is a compound based on PC+ABS Blend resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by ..
Tensile Strength at Break 96.0 MPa
13900 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS
LNP* THERMOCOMP* AF006XXZ is a compound based on ABS resin containing 30% Glass Fiber.
Tensile Strength at Break 96.0 MPa

@Temperature -40.0 °C
13900 psi

@Temperature -40.0 °F
ISO Data
Styrolution Luran® 358 N SAN
Luran 358 N is an easy-flowing injection molding SAN grade.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Tensile Strength at Break 96.0 MPa
13900 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp JF003L PES
LNP* Thermocomp* JF003L is a compound based on Polyethersulfone (PES) containing Glass Fiber. Characteristics of this grade are Low Extractable.This data was supplied by SABIC-IP for the Americas r..
Tensile Strength at Break 96.0 MPa
13900 psi
ASTM D638
Sumitomo Bakelite North America RX® 643 Fiberglass Reinforced Phenolic
RXÂ 643 is a fiberglass reinforced, ammonia-free, phenolic resole compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type GPI-10.Information pro..
Tensile Strength at Break 96.0 MPa
13900 psi
ASTM D638
BLUESTAR 403HF-G30 PBT, 30% Glass Filled
Typical Applications: Halogen Free; E/E connectors, socketsInformation provided by Polymer Technology and Services, LLC (PTS).
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HFD4412 PC (Europe-Africa-Middle East)
Lexan* HFD4412 is a 20% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Tensile Strength at Break 96.0 MPa
13900 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON OE002 PPS - LINEAR
LNP* STAT-KON* OE002 is a compound based on PPS - Linear resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.