- Polymer Property : Tensile Strength at Break = 1450 psi
Polymer Property : Tensile Strength at Break = 1450 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D412 |
| Polimeri Europa Europrene® SOL T 9131 Styrene - Isoprene Block Copolymer Europrene® SOL T 9131 is a linear block copolymer obtained by anionic polymerization. The polymer is based on styrene and isoprene, where bound styrene content is 15% weight and diblock content is.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527 |
| Polimeri Europa Flexirene® MS 26 A Linear Low Density Polyethylene Flexirene MS 26 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Parts made with Flexirene MS 26 A are characterized by optimum low tempe.. |
|||
| Tensile Strength at Break | <= 10.0 MPa | <= 1450 psi | ISO/R527 |
| Polykemi AB POLYelast TPE Z650A Thermoplastic Elastomer, SEBS-based, Co-injection Grade Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Rate of 50 mm/min; ASTM D 638 |
| NOVA Chemicals Surpass® IFs932-R Octene SLLDPE Injection Molding Resin IFs932-R complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food.NOVA Chem.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Injection molded parts; DIN 53504 |
| Huntsman IROGRAN® CA116-203 TPU-Polyester Introduction: IROGRAN CA116-203 is a high performance polyester based thermoplastic polyurethane intended for flat die extrusion applications. IROGRAN CA116-203 is part of the HUNTSMAN film and shee.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL WCP821 PPE-TPE (Europe-Africa-Middle East) Flexible Noryl* injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in over-molding applications such as plugs, strain .. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | |
| Shin-Etsu Silicones FEA-261U Fluorosilicone Elastomer ShinEtsu FEA261 U is one of a series of fluorosilicone compounds. It is designed to process well in molding applications. It can be blended with other members of the series for intermediate hardness.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | 500mm/min; ASTM D638 Type IV Specimen |
| Westlake EMAC® SP2207 20% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2207 is a 20% EMA copolymer designed for extrusion coating, tie-layers, and extrusions where flexibility, compatibility, low heat seal temperatures, or high coefficient of friction.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | at max load; ASTM D638 |
| A. Schulman CP775-01 Molding Grade, Low Density Polyethylene DescriptionCp 755-01 is a molding grade, low-density polyethylene. ApplicationCP 755-01 meets the specification contained in FDA Regulation 177.1520 for food contact applications.Information provid.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| ELASTO UK Dryflex® 420401S SBS Based Material, 40D Hardness, Natural The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| ELASTO UK Dryflex® 422401S SBS Based Material, 40D Hardness, Black The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
| Fainplast Compounds GS 55/KSN Flexible PVC, Injection Molding for Transparent Technical Items Cupping-glasses |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
| Fainplast Compounds GS 7016 Flexible PVC, Injection Molding for Footwear Soles for mild climates |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
| Fainplast Compounds GSO 70/33 Flexible PVC, Injection Molding for Footwear Soles, opaque surface |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | IEC 60811 |
| Fainplast Compounds HAX HF 019/27 Halogen Free PVC Sheathing; high flexibility |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Braskem PB681/59 LDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Lamination film; general purpose. Information provided by Braskem |
|||
| Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | |
| Beijing Evergrow Resources PTFE, 60% Bronze Filled Filled PTFE article is manufactured by molding method with filled PTFE resin. Filled PTFE resin is manufactured by compounding PTFE granular resin with filler. Broadly speaking PTFE compounds have t.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Arkema Group EVATANE® 28-40 Copolymer Ethylene - Vinyl Acetate EVATANE® 28-40 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 28-40 is stabilized with antioxidants. The High Vinyl Acetate co.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Arkema Group LOTADER® 5500 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 5500 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high pressure autoclave process. These grade is characterised by a high fluidity. Functional group.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Arkema Group LOTADER® 6200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 6200 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. Due to its properties (reactivity, fluidity), LOTADER 62.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Braskem EB 853 LDPE Cast Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Films for absorbents and diapers (with HDPE and LLDPE); general purpose. Information provi.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Teknor Apex APEX® 3311-60NT Polyvinyl Chloride, Flexible Features: Non-DEHP Plasticizer; Ethylene Oxide Sterilizable Uses: Medical/Healthcare Applications; Toys; Tubing Processing Method: Extrusion Forms: PelletsInformation Provided by Teknor Apex |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
| Fainplast Compounds PK 5510 Flexible PVC, Lead Free Profiles |
|||
| Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | |
| Beijing Evergrow Resources PTFE, 20% Glass Fiber Filled Filled PTFE article is manufactured by molding method with filled PTFE resin. Filled PTFE resin is manufactured by compounding PTFE granular resin with fillers of many different kinds. Amongst the m.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | |
| LATI Latiohm 52/11-10 PD02 PP Homopolymer Dissipative product based on Polypropylene homopolymer (PPh). Unfilled.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria T.. |
|||