Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 174 MPa | 25200 psi | 50 mm/min; ISO 527-1,2 |
Qualchem Danamid FCF-20 Polyamide 6, 20% Carbon Fiber Reinforced with carbon fiber, antistatic and conductive.Information provided by Qualchem Zrt. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stabi.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218G V33 Black 41N PA66, 33% glass fiber, DRY Description: TECHNYL® A 218G V33 Black 41N is a polyamide 66, reinforced with 33% of glass fiber, heat stabilized, for injection molding. The product is available in black color.Benefits: This pr.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp ICP36 PA 6/12 (Asia Pacific) LNP* Lubricomp* ICP36 is a compound based on Nylon 6/12 resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, , Electrically Conductive.This data was .. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp ICP36 PA6.12 LNP* Lubricomp* ICP36 is a compound based on Nylon 6/12 resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, , Electrically Conductive.This data was .. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP OCL36EXP PPS - LINEAR LNP* LUBRICOMP* OCL36EXP is a compound based on Linear PPS containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include; Wear Resistant, Electrically Conductive. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFP38 PA6.6 LNP* LUBRICOMP* RFP38 is a compound based on Nylon 66 containing 40% Glass Fiber, 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA), 25% Glass Fiber (Dry) Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional s.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF0069SF PA 66 LNP* THERMOCOMP* RF0069SF is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF0069SF PA 66 (Asia Pacific) LNP* Thermocomp* RF0069SF is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON EX07311P PEI (Asia Pacific) LNP Stat-kon* EX07311P is an easy flowing ESD-safe compound based on Polyetherimide resin. This compound is developed for good dimensional stability for use in ESD Tray for Backend Semicon and HDD t.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP EF006E PEI LNP THERMOCOMP* EF006E is a compound based on Polyetherimide resin containing 30% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R525H BK02 Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525H BK02 is high-flow, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when expose.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R525H BK0201 Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525H BK0201 is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical propertie.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R525H BLK Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525H BLK is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R525H Nylon 66, 25% Glass Filled, Dry as Molded Vydyne® R525H is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties whe.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Verton PV007SV_YW8D151 PA 6 Preliminary data for 35% long fiber single pellet color filled PA6This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | Type I, 5 mm/min; ASTM D638 |
LNP ULTEM® SMU5834 Polyetherimide, 20% Carbon Fiber Reinforcement
(discontinued **) High modulus with shielding/ conductive characteristics for high-heat applications.Features: Electrically Conductive, High Heat Resistance, High StrengthForms: PelletsProcessing Method: Injection Mo.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R525H Nat Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525H Nat is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties.. |
|||
Tensile Strength at Break | 174 MPa | 25200 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOTUF IX02582 PA 6/12 (Asia Pacific) LNP* Thermotuf* IX02582 is a compound based on Nylon 6/12 resin containing Proprietary Filler(s). Added features of this material include: High Impact. |