Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 20.0 MPa | 2900 psi | STN EN ISO 527-2 |
Plastcom PLASTALEN® PC 69 T 10 003/1M Polypropylene reinforced with mineral filler Modified PP copolymer for injection molding with the content of 10% mineral filler. Application in all automotive industry. Delivered in black.Information Provided by Plastcom spol. s r.o. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | 2 in/min; ASTM D638 |
RheTech Products FT2600-01UV Thermoplastic Polyolefin, UV Stabilized, Black Applications: Interior trimSplash shieldsStep pads and hitch padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | 2 in/min; ASTM D638 |
RheTech Products FT2700-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Air deflectorsFuel filler shieldsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527 |
Polyplastic Armlen® PP MF 40-3M Polypropylene Copolymer, 40% Calcium Carbonate Injection moldingInformation provided by PolyPlastic Group. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO.527 DIN.53455 |
Omnia Plastica PTFE Polytetrafluoroethylene A Fluoropolymer used mainly for its excellent chemical resistance. It has poor mechanical features. The strain, even under low weight, makes it very suitable as a gasket material.Features:Chemical: .. |
|||
Tensile Strength at Break | <= 20.0 MPa | <= 2900 psi | ISO/R527 |
Polykemi AB POLYfill PPC K5025 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP CL001I PS (Asia Pacific) LNP* Lubricomp* CL001I is a compound based on Polystyrene resin containing PTFE. Added features of this material include: Internally Lubricated, High Impact. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | 2 in/min; ASTM D638 |
RheTech Products M25P251-01 25% Mica Reinforced Polypropylene Copolymer, Black Applications: Fan shroudsGlove box binFiller panelsClose-out panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
3M Dyneon™ THV 220G Fluorothermoplastic
(discontinued **) THV 220G is a flexible, transparent fluoroplastic composed of tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride in the form of pellets. IT proves a balance of low temperature process.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | |
LATI Latene® 7H2-V2HF PP Homopolymer, Heat Stabilized, Flame Retardant Polypropylene homopolymer (PPh) based compound. Heat stabilized. UL94 V-2 classified, halogens-based flame retardants free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD825 PPE-TPE (Asia Pacific) Flexible, very low-migration, halogen-free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame retardant performance capable of meeting UL VW-1 re.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD841U PPE-TPE (Europe-Africa-Middle East) Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics SABIC PPCOMPOUND 7985 PP SABIC® PPcompound 7985 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with interior automotive UV stability. The IMDS is 2097.. |
|||
Tensile Strength at Break | 20.0 - 40.0 MPa @Thickness 2.00 mm |
2900 - 5800 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 11010 Polyvinylidene Fluoride (PVDF) Solef® 11010 PVDF is a medium-viscosity flexible PVDF copolymer resin and is typically processed by extrusion.Features: Copolymer; Good Flexibility; Medium ViscosityAdditional Properties: Crystal.. |
|||
Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | |
Sibur SKD-ND 4th Group Butadiene Rubber (BR) Buna CB 24. It is used in tires and the rubber and asbestos technical industries. It is combined with natural butadiene-styrene rubbers in any ratio, which is very important during production of a.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
Teknor Apex APEX® 3600-85NT Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Agency Ratings: NSF 61 Forms: Pellets Additional Information: First Generation SeriesInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
Teknor Apex APEX® 80853-A Polyvinyl Chloride, Flexible Notes: 105°C Insulation; RoHS Compliant Uses: Wire and Cable Applications Agency Ratings: UL QMTT2 .E73402 Forms: Pellets Wire Types: THHN; THW; TW; THHW; THWNInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
SCG Chemicals EL-Proâ„¢ P640J Polypropylene Injection Molding Key Characteristics:Good flowabilityHigh stiffnessHigh impact strengthRecommended Applications:High impact electrical appliance parts, automotive and motorcycle parts such as fan stand, washing tubI.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
UBE F022SE Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
Daikin POLYFLON M-391 PTFE Molding Powder, Free Flow Free flow powder.Processing Methods: Compression molding and automatic or semi-automatic compression molding.Features: Used if concerned about insufficient molding pressure for flat sheets.Informati.. |
|||
Tensile Strength at Break | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
Daikin POLYFLON MG-1040F PTFE 20% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow 20% glass fiber filled. High apparent density and free-flowing properties. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Availabl.. |
|||
Tensile Strength at Break | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
Daikin POLYFLON MG-1050F PTFE 25% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow 25% glass fiber filled. High apparent density and free-flowing properties. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Availabl.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
Azdel SuperLite® SL550600-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness) AZDEL SuperLite® SL550600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ASTM D4894 |
Adamas Adalon® 103 PTFE, 10% Carbon Filled Information provided by Adamas, HPM |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | cured; ISO 6922 |
3M Scotch-Weld™ EC40 General Purpose Instant Adhesive 3M™ Scotch-Weld™ General Purpose Instant Adhesives are single component, high strength ethyl cyanoacrylate adhesive designed to bond to a variety of substances including most plastics, rubbers, me.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527 |
Polimeri Europa Clearflex® RL 50 U Linear Medium Density Polyethylene Clearflex RL 50 U is a linear medium density polyethylene resin, with antioxidants and UV stabilizers, suitable for rotomolding applications.Items manufactured with Clearflex RL 50 U show good mecha.. |
|||
Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ISO R 527 |
Fainplast Compounds KL 93/1 Flexible PVC, Insulation for High Temperatures Lead Free Operatine temperature 105°C |
|||
Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ISO R 527 |
Fainplast Compounds KLT 93 Flexible PVC, Insulation Transparent Cables Lead Free Transparent cables (105°C) |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP CL001I PS LNP* Lubricomp* CL001I is a compound based on Polystyrene resin containing 5% PTFE. Added features of this material include: Internally Lubricated, High Impact. |
|||
Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | |
Beijing Evergrow Resources PTFE Extrusion Tube Features:PTFE extruded tubing is manufactured by high pressure PTFE dispense resin mixed with additive, it is extruded and sintered. According to different demands, the tubing could be opaque or tra.. |