Polymer Property : Tensile Strength at Break = 20000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Polymer Resources NY66-IMG33 Nylon, 33% Glass Reinforced, Impact Modified (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide..
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Polymer Resources NY66-IMG33-[color]H Nylon, 33% Glass Reinforced, Impact Modified, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide..
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Ravago Manufacturing Americas Hylon® N1033L Nylon 6/6 (Cond) (discontinued **) Information provided by Ravago.
Tensile Strength at Break	138 MPa	20000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFL36XXZ PA 66 (Asia Pacific) LNP Lubricomp is a compound based on PA66 resin containing glass fiber, PTFE. It is an internally lubricated compound that provide excellent chemical resistance, strength and wear/friction propertie..
Tensile Strength at Break	138 MPa	20000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP UX05051 PPA (Europe-Africa-Middle East) Internally lubricated Polyphthalamide compound, containing Glass Fiber and PTFE. Added features include Heat Stabilized, Flame Retardant and Hot Water Moldable
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Techmer ES PlaslubeÂ® J-4/30/TF/13/SI/2 BK223 PA6/12
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Sumitomo Bakelite North America EM 7302 Hardware Grade Epoxy Long fiberglass reinforced epoxy molding compound which features high strength and toughness for structural components. This compound is designed for applications requiring Mil-M-46069 certificatio..
Tensile Strength at Break	138 MPa	20000 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® PLS FR95G15DH2 BK269 Nylon 6 15% Glass Reinforced Flame Retardant Heat Stabilized Polyamide Zytel PLSFR95G15DH2 BK269 is 15% glass reinforced flame retardant black PA using SHIELD Technology only from DuPont exceptional resista..
Tensile Strength at Break	138 MPa	20000 psi	2.0 in/min; ASTM D638
LTL Color Compounds ColorFast® NY1GF330 Nylon 6, 33% Glass-Filled 33% glass-filled nylon 6All information provided by LTL Color Compounders, Inc.