Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Tensile Strength at Break = 20600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 142 MPa
20600 psi
ASTM D638
Network Polymers Kepital® F20-25
Description: Natural Acetal Copolymer, 25% Glass Reinforced GradeInformation provided by Network Polymers Inc.
Tensile Strength at Break 142 MPa
20600 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® LGK5030 PC (Asia Pacific)
Glass reinforced. Flame retardant.
Tensile Strength at Break 142 MPa
20600 psi
Lushan PA6+30% GF Nylon Toughener/PA Impact Modifier
Nylon toughener/PA impact modifier Lushan series is a maleic anhydride grafted polyolefin elastomer, with a very low residual maleic anhydride monomer, no irritating odor when using. Nylon toughener..
Tensile Strength at Break 142 MPa
20600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP JCL36 PES (Europe-Africa-Middle East)
LNP* LUBRICOMP* JCL36 is a compound based on Polyethersulfone resin containing Carbon Fiber, PTFE. Added features include : Internally Lubricated, Electrically Conductive.
Tensile Strength at Break 142 MPa
20600 psi
ISO 527 Type 1A
Solvay TECHNYL® A 60 G1 V25 PA66, 25% glass fiber, DRY
Description: TECHNYL® A 60G1 V25 is a 25% GF reinforced organophosphorous flame retarded grade based on a patented high flow polyamide 66 resin. This product is heat stabilized and provides optim..
Tensile Strength at Break 142 MPa
20600 psi
ISO 527 Type 1A
Solvay TECHNYL® C 538XT V30 Natural W PA6, 30% glass filled, DRY
Description: Polyamide 6 reinforced with 30% of glass fibers, heat stabilized, with high viscosity and high toughness, for extrusion.Available in: North America Product Applications: This product is..
Tensile Strength at Break 142 MPa
20600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM SF2260 PEI Blend (Asia Pacific)
High flow Ultem for thin wall application
Tensile Strength at Break 142 MPa
20600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DEL13PXC PC (Europe-Africa-Middle East)
LNP* Stat-kon* DEL13PXC is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Superior Molding.
Tensile Strength at Break 142 MPa
20600 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp DF008P PC
LNP THERMOCOMP* DF008P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the ..
Tensile Strength at Break 142 MPa
20600 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF006 PES
LNP* THERMOCOMP* JF006 is a compound based on Polyethersulfone resin containing 30% Glass Fiber.
Tensile Strength at Break 142 MPa
20600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF006 PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF006 is a compound based on Polyethersulfone resin containing Glass Fiber.
Tensile Strength at Break 142 MPa
20600 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC
LNP* Thermocomp* Lexan_LGN5030 compound is a glass reinforced. Flame retardant.
Tensile Strength at Break 142 MPa
20600 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC (Asia Pacific)
Glass reinforced. Flame retardant.
Tensile Strength at Break 142 MPa
20600 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC (Europe-Africa-Middle East)
LNP* Thermocomp* Lexan_LGK5020 compound is a glass reinforced, flame retardant material.
Tensile Strength at Break 142 MPa
20600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP JCL36E PES
LNP* LUBRICOMP* JCL36E is a compound based on Polyethersulfone (PES) resin containing 30% Carbon Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Tensile Strength at Break 142 MPa
20600 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp DF008P PC (Asia Pacific)
LNP* THERMOCOMP* DF008P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the..
Tensile Strength at Break 142 MPa
20600 psi
Toyobo ECOVYLOPET® EMC2330 PET Bottle Recycling Grade, 30% Glass Reinforced
Features: PET Bottle Recycling Grade, 30% Glass Fiber Reinforced, General PurposeApplications: Automobile engine head coversHot platesVending machine partsUmbrella ribsInformation provided by Toyobo..
Tensile Strength at Break 142 MPa
20600 psi
ASTM D638
Toyobo VYLOPET® EMC618P PBT/PET Alloy, Anti-microbial
Applications: Gas equipment partsFeatures: Good anti-microbialWarpagelessFlame resistantInformation provided by Toyobo.
Tensile Strength at Break 142 MPa

@Temperature 22.8 °C
20600 psi

@Temperature 73.0 °F
ASTM D638
Ensinger TECANYL™ MT CF30 Autoclavable Polymer
TECANYL™ MT is a new family of autoclavable materials developed for medical device applications. The material offers the desired performance properties of PPSU based resins with the machining ease..
Tensile Strength at Break 142 MPa
20600 psi
ISO 527-1/-2
DuPont Performance Polymers Sorona® 3030G BK001 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)&
30% Glass Reinforced Polytrimethylene Terephthalate Sorona 3030G BK001 is a 30% glass reinforced black PTT resin containing 25% renewably sourced ingredients by weight (37% polymer basis) with good ..
Tensile Strength at Break 142 MPa
20600 psi
ISO 527-1/-2
DuPont Performance Polymers Sorona® 3030GV BK001 Polytrimethylene Terephthalate (PTT)
30% Glass Reinforced Renewably Sourced Polytrimethylene Terephthalate Sorona 3030GV BK001 is a 30% glass reinforced black PTT resin containing 25% renewably sourced ingredients by weight (37% based ..
Tensile Strength at Break 142 MPa
20600 psi
DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66  (Unverified Data**)
33% Glass Reinforced Toughened Polyamide 66 Zytel 80G33L NC010 is a 33% glass fiber reinforced polyamide 66 resin with outstanding impact resistance developed using DuPont Super Tough technology.Inf..
Tensile Strength at Break 142 MPa

@Temperature 23.0 °C
20600 psi

@Temperature 73.4 °F
ISO 527
DuPont Performance Polymers Sorona® 3030G BK001 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)&
Sorona® 3030G BK001 is a 30% glass reinforced black PTT resin containing 25% renewably sourced ingredients by weight (37% polymer basis) with good strength, stiffness and low warpage and superior s..
Tensile Strength at Break 142 MPa

@Temperature 23.0 °C
20600 psi

@Temperature 73.4 °F
ISO 527
DuPont Performance Polymers Sorona® 3030GV BK001 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)
Sorona® 3030GV BK001 is a 30% glass reinforced black PTT resin containing 25% renewably sourced ingredients by weight (37% based on polymer only) with low warpage and superior strength, stiffness a..
Tensile Strength at Break 142 MPa
20600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON QE002S PA6.10
LNP* STAT-KON* QE002S is a compound based on Nylon 6/10 containing 10% carbon Fiber. Added features of this material include: Heat Stabilized, Electrically Conductive.
Tensile Strength at Break 142 MPa
20600 psi
ASTM D638
LG Chemical LUCON CP-4208F Conductive Thermoplastic, Flame Retardant
LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin..