Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
SABIC M40053S High Density Polyethylene for Injection Molding Product Description: M40053S is a UV stabilized high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to pro.. |
|||
Tensile Strength at Break | <= 21.0 MPa | <= 3050 psi | ISO/R527 |
Polykemi AB POLYfill PP CPQ10015 FF Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | >= 21.0 MPa | >= 3050 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM 825E High Impact Polystyrene Grade 825E is a high impact polystyrene designed specifically for extrusion and thermoforming. It is used for production of industrial packaging via deep draw thermoforming and custom multilayer sh.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO 527 |
Polimeri Europa Clearflex® RM 50 U Linear Medium Density Polyethylene Clearflex RM 50 U is a linear medium density polyethylene resin, with antioxidants and UV stabilizers, suitable for rotomolding applications.Items manufactured with Clearflex RM 50 U show good mecha.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
LyondellBasell Hifaxâ„¢ RTA3263EUV Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ RTA3263EUV fractional melt flow, 1,500 MPa flexural modulus, UV-stabilized, mineral-filled, extrusion grade thermoplastic elastomeric olefin (TEO) resin has an excellent com.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD771 PPE-TPE (Asia Pacific) Flexible, high tensile elongation, halogen-free extrusion grade intended for evaluation in applications such as cable jacket. Flame retardant performance capable of meeting UL VW-1 requirement. 80C .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD801AU PPE-TPE (Asia Pacific) Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP LNP* Lubricomp* MX91206 is a compound based on Polypropylene containing proprietary fillers. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP OL003A PPS - Branched LNP* LUBRICOMP* OL003A is a compound based on PPS - Branched resin containing 15% PTFE. Added features of this grade are: Wear Resistant. |
|||
Tensile Strength at Break | >= 21.0 MPa | >= 3050 psi | |
Shandong Dongyue Shenzhou New Material Co DS600 Perfluorinated Ethylene-Propylene Copolymer Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene resin is the copolymer of the TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Sterigenics Raprex® R-200 Branched High Density Polyethylene Applications: Injection Molding and ExtrusionRAPREX® R-200 is a high density polyethylene based resin that exhibits an excellent balance of melt processability and physical properties due to its .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Sterigenics Raprex® R200D Branched High Density Polyethylene Applications: Injection Molding and ExtrusionRAPREX® R200D is a high density polyethylene based resin that exhibits an excellent balance of melt processability and physical properties due to its .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp TH0450D PUR (Asia Pacific) LNP* Thermocomp* TH0450D is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.This data was supplied by .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD851 PPE-TPE (Asia Pacific) Flexible, strong flame-retardant, halogen-free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame retardant performance capable of meeting UL VW-.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp 2Z004 FP-E (EFTE) LNP* 2Z004 is a compound based on Ethylenetetrafluoroethylene (ETFE) containing Milled Glass.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 21.0 MPa @Treatment Temp. 145 °C, Time 2100 sec |
3050 psi @Treatment Temp. 293 °F, Time 0.583 hour |
Cure; ASTM D412 |
Styron Sprintan® SLR 4602 Solution Styrene Butadiene Rubber (S-SBR) Composition: SPRINTAN® SLR-4602 – Schkopau is manufactured by anionic solution polymerization using an organo-lithium initiator. The product has a medium styrene/high vinyl micro structure a.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
UBE R300 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO 527-2 |
Total Lumicene® mPE M 4041 UV Metallocene Polyethylene, Rotomolding Lumicene® mPE M 4041 UV is a new generation metallocene medium density polyethylene with hexene as comonomer.Lumicene® mPE M 4041 UV is intended for the manufacture of rotomolded items.Lumicene® .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO 527-2 |
Total PSI 7240 High Impact Polystyrene 7240 is a very high impact polystyrene for the extrusion industry. This grade has been designed to be diluted with crystal polystyrene (such as LACQRENE® 140, 1340 or 1540) at higher levels than c.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Toyobo PELPRENE™ P40H Polyester TPE Features: Polyester TPEInformation provided by Toyobo. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ CMW 203 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin characterized by high flow and designed for automotive interior applications such as door panel linings and other low pressure back mo.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Equate EMDA-8920 HDPE Injection Molding Resin EMDA-8920 is a high density copolymer polyethylene resin designed for injection molding applications which require excellent toughness and gloss.Applications: EMDA-8920 is a high density copolymer p.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D882 |
3M 25M25X Protective UV Tape 3M™ Protective UV Tape 25M25X is a proprietary, black and white co-extruded polyethylene tape for temporary outdoor and indoor protection of many metals, plastics and glass.Information provided by .. |
|||
Tensile Strength at Break | >= 21.0 MPa | >= 3050 psi | ASTM D4894 |
Adamas Adalon® 902 PTFE, 1% Conductive filler Information provided by Adamas, HPM |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO R 527 |
Addiplast Addilene J 120 M10 Polypropylene Copolymer Low fluidity for extrusion or injectionInformation provided by Addiplast. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Conditioned; ISO R 527 |
Addiplast Addilene J 490 M20F Flame Retardant Polypropylene, 20% Mineral Filled Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436M40L Mica Reinforced |
|||
Tensile Strength at Break | >= 21.0 MPa @Temperature 23.0 °C |
>= 3050 psi @Temperature 73.4 °F |
ASTM D1708 |
Solvay Specialty Polymers Hyflon® PFA M640 Perfluoroalkoxy (PFA)
(Unverified Data**) Hyflon PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resista.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |