Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 1.51 MPa | 219 psi | Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C |
3M AC-350 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are.. |
|||
Tensile Strength at Break | 1.51 MPa | 219 psi | Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C |
3M AC-350 Class B-12 Aerospace Sealant 3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are.. |
|||
Tensile Strength at Break | 1.51 MPa | 219 psi | Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C |
3M AC-350 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are.. |
|||
Tensile Strength at Break | 1.51 MPa | 219 psi | Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C |
3M AC-350 Class B-6 Aerospace Sealant 3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are.. |
|||
Tensile Strength at Break | 1.51 MPa | 219 psi | Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C |
3M AC-350 Class B-4 Aerospace Sealant 3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are.. |
|||
Tensile Strength at Break | 1.51 MPa | 219 psi | Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C |
3M AC-350 Class B-1/4 Aerospace Sealant 3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are.. |