Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 22.7 MPa | 3290 psi | Across Flow; DIN 53504 |
PolyOne OnFlex™ U 5365A-E0134 FG Thermoplastic Elastomer (TPE) OnFlex™ U 5365A-E0134 FG is a performance TPU alloy designed for use in injection molding application where FDA compliance and Overmolding onto PC, ABS and PC/ABS substrates are required.Properties.. |
|||
Tensile Strength at Break | 22.7 MPa @Treatment Temp. 145 °C, Time 2100 sec |
3290 psi @Treatment Temp. 293 °F, Time 0.583 hour |
Cure; ASTM D412 |
Styron Buna® SB 1739 Schkopau Cold Polymerized Emulsion Styrene Butadiene Rubber (E-SBR) Composition: Buna® SB 1739 – Schkopau is manufactured by cold polymerization using mixed rosin acid /fatty acid soaps. In relation to solid rubber it is plasticized with 37.5 parts of TDAE o.. |
|||
Tensile Strength at Break | 22.7 MPa | 3290 psi | ASTM D3759 |
3M 235 Photographic Tape 3M™ Photographic Tape 235 is a black colored opaque tape used in general purpose camera applications.Information provided by 3M |
|||
Tensile Strength at Break | 22.7 MPa | 3290 psi | Post cure 2 hours @ 232°C |
3M Dyneon™ FPO 3740 Fluoroelastomer 3M™ Dyneon™ FPO 3740 is a peroxide curable fluoroelastomer terpolymer containing 69.5 wt% fluorine. FPO 3740 can be used in compression, transfer or injection molding, and extrusion processes. Fea.. |
|||
Tensile Strength at Break | 22.7 MPa | 3290 psi | |
Asahi Glass Fluon® RB1020S 20% Glass Fiber, PTFE Filled Compound Fluon®PTFE FC has improved creep and wear resistance. A wide range of fillers such as glass fiber, graphite, bronze, carbon fiber are available. Information provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 22.7 MPa | 3290 psi | ASTM D3756 |
3M 1900 Specialty High Temperature Masking Tape 3M™ Value Duct Tape 1900 is a conformable cloth duct tape made with polyethylene film over cloth scrim and rubber adhesive. A good choice for non-critical applicationsInformation provided by 3M |