Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products CC30P100-01 30% Calcium Carbonate Reinforced Polypropylene, Black Applications: Consumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products FRP256-00 Polypropylene Copolymer, Flame Retardant, Natural Applications: Electrical component housingsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products FRp256-01 Polypropylene Copolymer, Flame Retardant, Black Applications: Electrical component housingsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products P252-01 Polypropylene Copolymer, Black Applications: Cowl screenInterior trimBumper coverGlove box binInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products RCT140-01A 40% Talc Reinforced Polypropylene, Black, Recycled Content Applications: HVAC ductworkI/P componentsFuse panel assembliesUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products RCT220-01 20% Talc Reinforced Polypropylene Copolymer, Black, Recycled Content Applications: Fan shroudsElectrical housingsHush panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products T10P250-00 10% Talc Reinforced Polypropylene Copolymer, Natural Applications: Fan shroudsCenter consolesAir ductsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products T20P252-00 20% Talc Reinforced Polypropylene, Natural Applications: IP Structural componentsGlove box binWire troughInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products T20P252-01 20% Talc Reinforced Polypropylene Copolymer, Black Applications: IP Structural componentsGlove box binWire troughInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | ASTM D638 |
Network Polymers NPP 50-0350 Description: High Density Polyethylene (HDPE)Information provided by Network Polymers Inc. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | chs 2 in/min; ASTM D638 |
Network Polymers NPS 80-1410 Polystyrene Description: Injection Molding Grade, Medium Impact, High Melt FlowInformation provided by Network Polymers Inc. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
Ineos H44N-00 Polypropylene Homopolymer H44N-00 is a high flow rate, nucleated polypropylene homopolymer designed for compounding and injection molding applications. The grade benefits from a high stiffness and isotropic shrinkage to help.. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | ASTM D638 |
Chesterton ARC SD4i High temperature ceramic reinforced erosion resistant coating Description: An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10-15 mils) per coat.. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | vs. rigid PVC; 10 s set time |
Elmer's Products Aron Alpha® 432TW Cyanoacrylate Adhesive (Industrial Krazy Glue™) Extra tough adhesives with highest heat, peeling, impact and thermal shock resistance.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Fa.. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | vs. aluminum; 3 s set time |
Elmer's Products Aron Alpha® 801 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Low odor, low chlorosis (bloom) when a transparent bond, appearance and strength are required.Low gap fill. Ethoxyethyl monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. .. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | vs. rigid PVC; 5 s set time |
Elmer's Products Aron Alpha® GEL 10 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DMDB-7950 NT 7 High Density Polyethylene Resin DOW DMDB-7950 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as roll-out trash carts and other large parts with short mo.. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | ASTM D882 |
3M 15CV826 General Purpose Temporary Surface Protection Tape 3M™ General Purpose Temporary Surface Protection Tape 15CV826 is a medium adhesion temporary protection tape designed for a variety of surface protection applications.Information provided by 3M |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | ASTM D638 Die C |
3M Scotch-Weld™ TE030 Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as .. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | |
Abatron AboCast 8501-6 One-Component Epoxy AboCast 8501-6 is a clear, high-temperature one-component epoxy system for very high-temperature uses. It offers the highest heat resistance of the clear resins. Suggested Uses: Casting; Potting; E.. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | TM R050-36 |
Resinlab® EP1300 Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1300 Clear (Formerly Lab Product W092602) is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It has a pot life of about one hour and .. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
RheTech Products CC30P100-00 30% Calcium Carbonate Reinforced Polypropylene, Natural Applications: Consumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 26.2 MPa | 3800 psi | ASTM D638 ISO 527-2 |
DuPont Elvax® CM4875 Ethylene Vinyl Acetate
(discontinued **) DuPont™ Elvax® CM4875 is an ethylene-vinyl acetate copolymer resin for use in industrial applications. Specialty grades of Elvax® have the unusual combination of high vinyl acetate levels and low.. |