Polymer Property : Tensile Strength at Break = 28.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 28.3 MPa
4100 psi
2 in/min; ASTM D638
RheTech Products T40P100-04 40% Talc Reinforced Polypropylene, White
Applications: Automotive componentsConsumer productsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 28.3 MPa
4100 psi
2 in/min; ASTM D638
RheTech Products T40P105-04 40% Talc Reinforced Polypropylene, White, 5% Titanium Dioxide
Applications: Instrument cluster masksAutomotive componentsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Niche Polymer PPCT20BK Copolymer PP, 20% Talc Filled
Information provided by Niche Polymer
Tensile Strength at Break 28.3 MPa
4100 psi
2 in/min; ASTM D638
RheTech Products HP516-01 7% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black
Applications: Interior trimCenter consolesHush panelsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
LyondellBasell Petrothene® GA837091 Medium Density Polyethylene  (Unverified Data**)
ApplicationsPETROTHENE GA 837-091 is a broad molecular weight, medium density resin designed for use as a base resin in wire and cable jacketing. An antioxidant has been added to ensure thermal st..
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 16% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 16% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B9001-16H , 16% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM-D638
Ineos ABS Lustran® Guardian™ 732 ABS, Extrusion Grade
Lustran® Guardian™ ABS 732 is an extrusion grade resin designed for use in thermoformed refrigerator and freezer liner applications. It is suitable for use with 245fa PU foams.
Tensile Strength at Break 28.3 MPa

@Treatment Temp. 145 °C,
Time 2100 sec
4100 psi

@Treatment Temp. 293 °F,
Time 0.583 hour
Cure; ASTM D412
Styron Buna® SB 1500 Schkopau Cold Polymerized Emulsion Styrene Butadiene Rubber (E-SBR)
Composition: Buna® SB 1500 – Schkopau is manufactured by cold polymerization using a rosin acid soap. A discoloring stabilizer is added during the production process.Application: Buna® SB..
Tensile Strength at Break 28.3 MPa
4110 psi
ASTM D882
Westlake Plastics PMP Film Made from TPX® Polymethylpentene Resin
Lowest specific gravity of any known thermoplastic. Exceptional electrical properties. Good chemical resistance. High heat resistance. Excellent acoustical properties. Transparency. FDA compli..
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Plastics Group Polifil® RMT-20 20% Talc-Reinforced Polypropylene, High Impact
Polifil® RMT series compounds are high impact polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and high heat deflection resis..
Tensile Strength at Break 28.3 MPa
4100 psi
vs. steel; 100 s set time
Elmer's Products Aron Alpha® 203 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair o..
Tensile Strength at Break 28.3 MPa
4100 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DMDA-8965 NT 7 High Density Polyethylene Resin
DOW DMDA-8965 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as food containers. Information provided by Dow
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Chesterton ARC MX2 High Wear Fine Particle Wear Compound
Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”..
Tensile Strength at Break 28.3 MPa
4110 psi
ASTM D3759
3M Scotch® 265 Fine Line Tape
Scotch® Fine Line Tape 265 is a high-performance film backed tape designed for in-mold fine line masking where sharp, clean, gel-coat color separation lines are desired.Information provided by 3M
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Plastics Group Polifil® T-10 10% Talc-Reinforced Polypropylene
Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colora..
Tensile Strength at Break 28.3 MPa
4100 psi
2 in/min; ASTM D638
RheTech Products CC20P100-01 20% Calcium Carbonate Reinforced Polypropylene, Black
Applications: ElectronicsConsumer GoodsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 16% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 28.3 MPa
4100 psi
Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable W9200 Polyvinyl Chloride, Flexible (PVC, Flexible)
Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 16% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 28.3 MPa
4100 psi
2 in/min; ASTM D638
RheTech Products CC20P100-00 20% Calcium Carbonate Reinforced Polypropylene, Natural
Applications: ElectronicsConsumer GoodsInjection molding conditions reported in table.Information provided by RheTech Products.