Polymer Property : Tensile Strength at Break = 370 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 2.55 MPa

@Temperature 121 °C,
Time 605000 sec
370 psi

@Temperature 250 °F,
Time 168 hour
3M AC-350 Class B-1/2 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 2.55 MPa

@Temperature 121 °C,
Time 605000 sec
370 psi

@Temperature 250 °F,
Time 168 hour
3M AC-350 Class B-12 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 2.55 MPa

@Temperature 121 °C,
Time 605000 sec
370 psi

@Temperature 250 °F,
Time 168 hour
3M AC-350 Class B-2 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 2.55 MPa

@Temperature 121 °C,
Time 605000 sec
370 psi

@Temperature 250 °F,
Time 168 hour
3M AC-350 Class B-6 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 2.55 MPa

@Temperature 121 °C,
Time 605000 sec
370 psi

@Temperature 250 °F,
Time 168 hour
3M AC-350 Class B-4 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 2.55 MPa

@Temperature 121 °C,
Time 605000 sec
370 psi

@Temperature 250 °F,
Time 168 hour
3M AC-350 Class B-1/4 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..