Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D638 |
Ravago Manufacturing Americas Enviramid™ N1300STHL Post Consumer Recycle Nylon 66 Superior Toughness, Heat Stabilized, Lubricated, Black and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D638 |
Polymer Resources PPX-GP8 Modified-PPO, Impact Modified Modified-Polyphenylene Oxide, Impact Modified, 240F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D638 |
Polymer Resources TP-FR IM PBT, Impact Modified, Flame Retardant, Low Flow Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D638 |
Polymer Resources TP-FR-IM Polybutylene Terephthalate, Impact Modified, Flame Retardant, Low Flow Polybutylene Terephthalate, Impact Modified, Flame Retardant, Low FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sa.. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | TM R050-36 |
Resinlab® EP1325LV Thixotropic, Heat Curing Epoxy Adhesive Resinlab™ EP1325 and EP1325LV are one part thixotropic, heat curing epoxy adhesives. They can also be used as a small mass potting compounds, staking or damming adhesives, or polymer systems where .. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | TM R050-36 |
Resinlab® EP1390 Medium Viscosity, Self Extinguishing Flame Retardant Epoxy Casting Resin System Resinlab™ EP1390 is a RoHS compliant, medium viscosity, self extinguishing flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Labor.. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D638 |
LNP Lubricomp® GFL-4034 EM M Polysulfone, Milled Glass Fiber Reinforcement, PTFE Lubricant
(discontinued **)& Features: Good Moldability, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP g.. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D412 |
Huntsman KRYSTALFLEX® PE 399 Polyurethane Optical Aliphatic Film Key Properties:Moisture ResistanceChemical CompatibilityCooler ProcessingHigher AdhesionMultiple Design OptionNo special storage requiredInformation provided by Alliance Polymers |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D638 |
DuPont Surlyn® SG201U NC010 Supergloss Molding Alloy Surlyn® SG201U is a modified ionomer resin for applications that require a high gloss, molded in color surface color surface finish directly from the mold. The material is weatherable, durable, an.. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D638 |
Plastics Group Polifil® GFPP-20 20% Glass-Reinforced Polypropylene Polifil® GFPP series compounds are homopolymer polypropylene resins reinforced with glass fibers. They provide high impact with increased strength, stiffness, surface hardness, and higher continuou.. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D638 |
Entec Hyrene® PSCRY 8 General Purpose Polystyrene Available in North America Features: General PurposeRoHS Compliant Form: Pellets Information provided by Entec |
|||
Tensile Strength at Break | >= 44.8 MPa | >= 6500 psi | |
3M Scotchcal™ 8662 Graphic Film This is a 2-mil, durable, opaque film designed for making short term graphics that are applied to unsealed, outdoor, pedestrian traffic surfaces or selected smooth-to-rough wall surfaces. This film .. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | 89% Ret. |
UBE UBESTA® 3030U Nylon 12 (After Isopropanol for 500 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c.. |
|||
Tensile Strength at Break | 44.8 MPa | 6500 psi | TM R050-36 |
Resinlab® EP1026 Black Epoxy Adhesive Resinlab™ EP1026 Black is a two part unfilled epoxy adhesive designed for high speed bonding of metals, ceramics, and most plastics. It cures to a tough semi-rigid material, and is free flowing in .. |