Polymer Property : Tensile Strength at Break = 49.6 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	49.6 MPa	7200 psi
Indium Corp. IndalloyÂ® 256 96.5Sn/3.0Ag/0.5Cu Lead-Free Solder Alloy Referred to as the SAC305 alloy.Information provided by the manufacturer, Indium Corporation.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D412
Compuestos Dominicanos Polycom PT-109599 PVC Description: Polycom rigid PVC compounds for the extrusion of pipes have excellent processing characteristics and are available in the form of pellets and dry blend. They are available with lead and..
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
Americas Styrenics EA3130 High Heat Crystal Polystyrene Product CharacteristicsAdditive FreeFood Contact CompliantTypical ApplicationsMedical PartsColor Concentrate CarrierLow Profile AdditivesInformation provided by AmericasStyrenics LLC.
Tensile Strength at Break	49.6 MPa	7200 psi
Abatron AboCast/AboCure 4-4/50-12 Casting Epoxy for Tooling Standard casting compound for molds or patterns of any size, that can be machined with common metal working tools, engraving and reproduction molds.Main Advantages: FastBest rigid, chemical, and hea..
Tensile Strength at Break	49.6 MPa	7200 psi	ASTM D638
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	49.6 MPa	7200 psi	2 in/min; ASTM D638
RheTech Products F24-01 20% Glass Fiber/Mineral Co-Reinforced Polypropylene Copolymer, Chemically Coupled, Black Applications: Head lamp housingsBracketsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.