Polymer Property : Tensile Strength at Break = 55.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	50.0 - 55.0 MPa	7250 - 7980 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_7210 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide ..
Tensile Strength at Break	50.0 - 55.0 MPa	7250 - 7980 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_7220 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide ..
Tensile Strength at Break	50.0 - 55.0 MPa	7250 - 7980 psi	ASTM D683
Loxim 500 00HB Polycarbonate/Acrylonitrile Butadiene Styrene Information provided by Loxim Industries
Tensile Strength at Break	50.0 - 55.0 MPa	7250 - 7980 psi	ASTM D683
Loxim 500 00V0 Polycarbonate/Acrylonitrile Butadiene Styrene Information provided by Loxim Industries
Tensile Strength at Break	41.0 - 55.0 MPa	5950 - 7980 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATG 115 Phenolic Molding Organic Filler, Compression Molded Characteristics:Medium mechanical strength Medium electrical insulationGeneral purposeColor- Black, BrownSoft/medium flow Applications: Electrical accessories & fittings ( medium quality ) Domestic ..
Tensile Strength at Break	46.0 - 55.0 MPa	6670 - 7980 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATS 1613-R Phenolic Molding Nylon and glass Filler, Compression Molded Characteristics:High dielectric & mechanical strengthWeather resistant Good electric insulationLow water absorption Good mechanical tension bearing capacityColor-blackMedium flow Applications:Railwa..
Tensile Strength at Break	38.0 - 55.0 MPa	5510 - 7980 psi	ASTM D638
Arkema Group KYNAR® 370 Polyvinylidene Fluoride (PVDF) Homopolymer - Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. Low melt shrinkage, graphite powder filled. High stability in harsh thermal, chemical and ultraviolet environments. High toug..
Tensile Strength at Break	34.0 - 55.0 MPa	4930 - 7980 psi	ASTM D638
Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness ..
Tensile Strength at Break	34.0 - 55.0 MPa	4930 - 7980 psi	ASTM D638
Arkema Group KYNAR® 740 Black/Red Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistance; high purityAppli..
Tensile Strength at Break	34.0 - 55.0 MPa	4930 - 7980 psi	ASTM D638
Arkema Group KYNAR® 740 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili..
Tensile Strength at Break	34.0 - 55.0 MPa	4930 - 7980 psi	ASTM D638
Arkema Group KYNAR® 740-02 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mecha..
Tensile Strength at Break	34.0 - 55.0 MPa	4930 - 7980 psi	ASTM D638
Arkema Group KYNAR® 760 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili..
Tensile Strength at Break	46.0 - 55.0 MPa	6670 - 7980 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATG 112 Phenolic Molding Organic Filler, Compression Molded Characteristics:Medium mechanical strength Medium electrical insulationGeneral purposeColor- Black, BrownSoft/medium flow Applications: Electrical accessories & fittings ( medium quality ) Domestic ..
Tensile Strength at Break	46.0 - 55.0 MPa	6670 - 7980 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Compression Molded Characteristics:Ammonia freeGood mouldabilityGood mechanical strengthGood electrical insulationGood surface finishMedium thermal stability Color-black, brownSoft/medium flow Applications:Telecommuni..
Tensile Strength at Break	46.0 - 55.0 MPa	6670 - 7980 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Injection Molded Characteristics:Ammonia freeGood mouldabilityGood mechanical strengthGood electrical insulationGood surface finishMedium thermal stability Color-black, brownSoft flow Applications:Telecommunication ..
Tensile Strength at Break	34.0 - 55.0 MPa	4930 - 7980 psi	ASTM D638
Arkema Group KYNAR® 720, 720 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness ..
Tensile Strength at Break	50.0 - 55.0 MPa	7250 - 7980 psi	ASTM D683
Loxim 830 01 HB Polypropylene Compound, Flame Retardant Information provided by Loxim Industries