Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY HRA222 ASA+PC (Europe-Africa-Middle East) GELOY HRA222 is a multi-purpose, chlorine and bromine free flame retardant ASA+PC alloy for injection moulding processes. Typical properties as measured on natural material. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY HRA222F ASA+PC Geloy HRA222F is a multi-purpose, chlorine and bromine free flame retardant PC+ASA alloy for injection molding processes. F1 rating according UL746C. Use for exterior/interior electrical application.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY HRA222F ASA+PC (Asia Pacific) Geloy HRA222F is a multi-purpose, chlorine and bromine free flame retardant PC+ASA alloy for injection molding processes. F1 rating according UL746C. Use for exterior/interior electrical application.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 915AU PC (Asia Pacific) LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® 915AU PC (Europe-Africa-Middle East) LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 9945A PC Lexan* resin 9945A Polycarbonate (PC)is a non-filled, injection moldable grade. This non-chlorinated, non-brominated PC has an UL-94 V0 rating at 1.8 mm. Lexan resin 9945A is available in clear tr.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® FXD103 PC FXD103 is a Light Diffusion effect, part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace.This data was supplied by SABIC-IP for the .. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXD103R PC (Asia Pacific) FXD103R is a Light Diffusion effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package may affect propert.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXD103R PC (Europe-Africa-Middle East) FXD103R is a Light Diffusion effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package may affect propert.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® FXD9945A PC (Asia Pacific) UV stabilzed Visualfx FR PC with non-brominated and non-chlorinated flame retardant systems. It is available Only in white diffused effect(WH8B111X) meeting UL-94 V0 at 2mm for thin wall application.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXD1413T PC Copolymer Clear PC-siloxane copolymer with excellent processability, in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may af.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL V01525 PPE+HIPS (Asia Pacific) Noryl* V01525 is a 15% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP AF002 ABS LNP THERMOCOMP* AF002 is a compound based on ABS resin containing 10% Glass Fiber. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MX95319 PP LNP* THERMOCOMP* MX95319 is a compound based on Polypropylene resin containing Proprietary Filler(s). |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT LNP* THERMOCOMP* WFB54 is a compound based on PBT resin containing 20% Glass Fiber, 25% Glass Bead. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH7111E PPE+HIPS Noryl* EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR a.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon IS000LX PA6.12 LNP* Stat-Kon* IS000LX is a compound based on Nylon 6/12 containing Stainless Steel Fibers.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® SHF4910 PBT (Europe-Africa-Middle East) 6.5% glass reinforced, Super High Flow, flame retardant PBT. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP AF002XXC ABS LNP THERMOCOMP* AF002XXC is a compound based on ABS resin containing 10% Glass Fiber. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER (Asia Pacific) Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER (Asia Pacific) Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ISO 527-2/50 |
Styron CALIBREâ„¢ 200-23 Polycarbonate Resin Overview: CALIBREâ„¢ 200-23 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistanc.. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MF004S PP LNP THERMOCOMP* MF004S is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66 LNP* THERMOCOMP* RB006 is a compound based on Nylon 66 resin containing 30% Glass Bead. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66 (Asia Pacific) LNP* Thermocomp* RB006 is a compound based on Nylon 66 resin containing Glass Bead. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl PX0346 PPE+PS This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
Aclo Accutech Polycarbonate POL050G10L Glass Reinforced |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | ISO 527 - 1 & - 2 |
Asahi Kasei Tenac® 4012 Homopolymer Acetal Resin Medium viscosity grade, with reduced stiffness and increased elongation through addition of special polymersInformation provided by Asahi Kasei Corporation. |
|||
Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER (Europe-Africa-Middle East) Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts.. |