Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® C1204HF PC+ABS (Europe-Africa-Middle East) High heat PC/ABS blend offering good flow and excellent impact. Food compliant according to FDA and European directive 2002/72/EC. Available in limited colors. Effective January 15th, 2008 this gra.. |
|||
Tensile Strength at Break | <= 47.0 MPa | <= 6820 psi | ISO/R527 |
Polykemi AB POLYabs X00 ABS, Extrusion Grade Information provided by Polykemi AB |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® C8080REC PC+ABS PC+ABS Recycle Resin with good flow, good temperature resistance and moderate impact |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CP8930 PC+ABS High heat, PC/ABS for automotive electro plating applications, excellent balance in flow/impact |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® CP8930 PC+ABS (Europe-Africa-Middle East) High heat, PC/ABS for automotive electro plating applications, excellent balance in flow/impactThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® HC1204HF PC+ABS (Asia Pacific) High heat PC/ABS blend offering good flow and excellent impact. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL4016H PC Copolymer (Europe-Africa-Middle East) 6% GF reinforced opaque polycarbonate-siloxane copolymer with good impact strength, stiffness and hydrolytic stability. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXM1414T PC Copolymer (Asia Pacific) PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXM1414T PC Copolymer (Europe-Africa-Middle East) PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.This data was supplied by .. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics GELOY XTPMFR10 ASA+PC (Asia Pacific) Improved ASA/PC blend for high flow, 1.0mm V0 applications. Improved UV performance aesthetically and physically compared to alternatives. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® BFL4000U PC Lexan* BFL4000U Polycarbonate resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating and good impact/flow balance. Designed fo.. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 10mm/min; ASTM D638 |
Kingfa PBT-T30 30% Mineral Filled PBT Features:Excellent size stabilityLow tendency to wrapLow abrasionGood surfaceApplications:Injection moldingApplication partsE & E partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KL003 Acetal Copolymer (Asia Pacific) LNP* LUBRICOMP* KL003 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copoly (Asia Pacific) LNP* Lubricomp* KL004L is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RL0049S PA 66 LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Halar® 500LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Low ViscosityUses: Wire & Cable ApplicationsAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 °CInformation prov.. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DX12411C PC LNP* STAT-KON* DX12411C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® IQ1103 PBT+PC (Europe-Africa-Middle East) Xenoy iQ*1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ* PBT (polybuty.. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® IQ1103U PBT+PC Xenoy* Resin iQ1103U - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103U is an unreinforced, UV stable, impact modified PC+ iQ-PBT alloy with excellent low temp.. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON RX08408 PA 66 LNP* STAT-KON* RX08404 is a compound based on Nylon 66 containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon RX08408_NA1D004 PA 66 LNP* Stat-Kon* RX08404_NA1D004 is a compound based on Nylon 66 containing Carbon Powder. Characteristics of this grade include: Electrically Conductive, High Impact.This data was supplied by SABI.. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP WX05456 Polyester, TP LNP THERMOCOMP* WX05456 is a compound based on Polyester, TP resin containing Mineral. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL N190X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. RTI Elec/Imp/Str 95/80/95. Dielectric strength. Suitable for E/E market applications. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON KD000 Acetal Copolymer LNP* STAT-KON* KD000 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 5E003M FP-V (PVDF) LNP* THERMOCOMP* 5E003M is a compound based on PVDF resin containing 15% Milled Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 |
Eastman Eastar MN004 Copolyester Eastar Copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN004 contains a mold release.Appl.. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527-1,-2 |
Covestro Bayblend® T65 HG PC/ABS Blend Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Injection molding, easy .. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | ASTM D412 |
Alliance Polymers Zythane™ 4080A Thermoplastic Polyurethane Elastomer Zythane™ 4080A is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good .. |
|||
Tensile Strength at Break | 47.0 MPa | 6820 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 11008/0001 Polyvinylidene Fluoride PVDF is ideal for multiple applications across a wide array of industries. Widely used in the chemical processing, wire and cable, semiconductor, and oil and gas industries. PVDF is also gaining rec.. |