Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 7.00 MPa | 1020 psi | ISO 37 |
PolyOne OnFlex™ S HF 90A-3S1988 Thermoplastic Elastomer (TPE) OnFlex™-S HF thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds utilize a unique, patent pending halogen free flame retardancy system. Fu.. |
|||
Tensile Strength at Break | 7.00 - 11.0 MPa | 1020 - 1600 psi | ASTM D412 |
Proto3000 Objet Digital Materials™ DM_9130/9430/9230/9330 Rubber-like Prototyping Polymer Primary material: TangoBlackSecondary material: VeroWhitePlus, VeroBlue, VeroBlack, FullCure720Digital Materials are made up of two Objet materials. The two materials are combined in specific concen.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCP761 PPE-TPE Flexible Noryl injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain re.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCP761 PPE-TPE (Asia Pacific) Flexible Noryl injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain re.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY M3000 PP LNP STAT-LOY* M3000 is a compound based on unfilled Polypropylene resin. Added feature of this material is: Antistat. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EMAC® SP2220 20% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2220 is a 20% EMA copolymer designed for compounding, extrusion coating, tie-layers, and extrusions where flexibility, compatibility, low heat seal temperatures, or high coefficien.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
ELASTO UK Dryflex® 500600S SEBS Based Material, Unfilled Qualities, 60A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
ELASTO UK Dryflex® 600650S SEBS Based Material, Filled Qualities, 65A Hardness, Natural The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material .. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
ELASTO UK Dryflex® 602650S SEBS Based Material, Filled Qualities, 65A Hardness, Black The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material .. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
ELASTO UK Dryflex® 660600S SEBS Based Material, Semi-Filled Qualities, 60A Hardness, Natural The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
ELASTO UK Dryflex® 662650S SEBS Based Material, Semi-Filled Qualities, 65A Hardness, Black The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
ELASTO UK Mediprene™ 500520M TPE, Medical Applications, 52A Hardness All Mediprene™ compounds are designed and manufactured for use in medical and pharmaceutical applications. In both medical and food contact areas, high application demands are found, such as:Low e.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ISO R 527 |
Fainplast Compounds GS 6612 Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
Arkema Group LOTRYL® 28 MA 07 Copolymer Ethylene - Methyl Acrylate LOTRYL® 28 MA 07 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the high methyl acrylate content, LOTRYL® 28 MA 07 is a polyme.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (9 mm Molded Thickness) AZDEL SuperLite® SL551600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (10 mm Molded Thickness) AZDEL SuperLite® SL551800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ISO 527-1 |
Barlog Plastics KEBAFLEX SG 65 A.01 TPE-S, Shore A65, natural TPE-SInformation provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
Arkema Group EVATANE® 40-55 Copolymer Ethylene - Vinyl Acetate EVATANE® 40-55 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. It’s stabilized with antioxidants and contains slip and antiblock additiv.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
Arkema Group EVATANE® 18-150 Copolymer Ethylene - Vinyl Acetate EVATANE® 18-150 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 18-150 is stabilized with antioxidants. The High Vinyl Acetate .. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
Petroquimica Triunfo Trithene® JX 7300 LDPE - Injection Molding The Trithene® JX 7300 resin is a low-density polyethylene (LDPE) with outstanding flow ability and flexibility. Those attributes are especially important to meet the requirements for fast injection.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (7 mm Molded Thickness) AZDEL SuperLite® SL551200-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (8 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 7.00 MPa | 1020 psi | |
Zelfo Technology Zelfo® HG Cellulose Fiber Material Zelfo® is a high performance bio-based material. Patented fibre technology developed by Zelfo Technology transforms 100% renewable or recycled cellulose fibres and water into self-binding Zelfo mat.. |