Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 72.4 MPa | 10500 psi | 2 in/min; ASTM D638 |
RheTech Products G40P100-00 40% Glass Fiber Reinforced Polypropylene, Natural Injection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Oxford Polymers ABS 30GF-BK ABS, 30% Glass Fiber Reinforced Product Description: Glass Fiber (30% Reinforced), ABS injection molding grade Processing and Delivery Form: Pellets and Injection Molding Additives: Release AgentsSpecial Characteristics: Pre-colo.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Polymer Resources PPX-G10 Modified-PPO, 10% Glass Reinforced Modified-Polyphenylene Oxide, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Polymer Resources TP-GFMF2 Polybutylene Terephthalate, 40% Glass/Mineral Reinforced Polybutylene Terephthalate, 40% Glass/Mineral ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informat.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Polymer Resources TPSF-G10 Polybutylene Terephthalate, Structural Foam, 10% Glass Reinforced Polybutylene Terephthalate, Structural Foam, 10% Glass ReinforcedProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Info.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Polymer Resources PC/TP-GP2-G20 PC Polyester, Excellent Chemical Resistance, 20% Glass Filled
(Unverified Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
M. Holland Company PC406R Polycarbonate Good impact resistanceGood mold releaseHigh viscosityApplications: AppliancesProtective coveringsDecorative displaysHousings |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Techmer ES Electrafil® NY-7/EC NAT PA6 |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 200-3 Polycarbonate Resin Overview: CALIBREâ„¢ 200-3 polycarbonate resin is produced in compliance with the US Food and Drugs Administration (FDA) and EU food contact regulation. This resin provides excellent impact resis.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 300-6 Polycarbonate Resin Overview: CALIBREâ„¢ 300-6 polycarbonate resin offer exceptional impact resistance, heat distortion resistance, and optical clarity as high melt strength for blow molding and sheet applications. .. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 303V-6 Polycarbonate Resin Overview: CALIBREâ„¢ 303V-6 Polycarbonate resins offer exceptional impact resistance and heat distortion resistance, and meets UL94 V-2 rating. CALIBRE 303V-6 contains a mold release agent, a UV .. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Chase Plastics CP Pryme® A120 ABS, 20% Glass Fiber Reinforced Features: Glass fiber reinforcementInjection moldingForm: PelletsInformation provided by Chase Plastics. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D3574 |
3M 435 Vibration Damping Tape 3M™ Vibration Damping Tapes are low temperature 3M™ Viscoelastic Damping Polymers Tape 830 coated on the dead soft aluminum foil constraining layer. They have pressure sensitive properties and are.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D3574 |
3M 436 Vibration Damping Tape 3M™ Vibration Damping Tapes are low temperature 3M™ Viscoelastic Damping Polymers Tape 830 coated on the dead soft aluminum foil constraining layer. They have pressure sensitive properties and are.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Polymer Resources PPX-G10 Modified PPO, 10% Glass Reinforced
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |