Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® C2100HF PC+ABS (Europe-Africa-Middle East) CYCOLOY C2100HF is a flame retardant blend with improved flow, specially developed to meet the stringent requirements of mains current carrying applications.This data was supplied by SABIC-IP for th.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol.. |
|||
Tensile Strength at Break | 50.0 - 60.0 MPa | 7250 - 8700 psi | ASTM D638-03 |
Proto3000 Objet Digital Materials™ DM_Dots_7513 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide t.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® CX5640 PC+ABS (Asia Pacific) Cycoloy* CX5640 is a all purpose PC+ABS blend specially developed for applications requiring weld line strength. High heat resistance combined with good flow, excellent impact and low temperature du.. |
|||
Tensile Strength at Break | <= 50.0 MPa | <= 7250 psi | ISO/R527 |
Polykemi AB POLYlux 4010 MP PC/PBT-Blend Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 50.0 MPa | <= 7250 psi | ISO/R527 |
Polykemi AB SCANTEC PC 85FR Polycarbonate, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HF1140R PC (Europe-Africa-Middle East) LEXAN HF1140R is a high flow grade. This material is especially designed for applications that require thin wall sections and high flow lengths. FDA food contact compliant in limited colors.Effect.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® LSHF PC (Asia Pacific) Clear PolyCarbonate, High Flow, UV Stabilization, Heat Stabilization |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® LSHF PC (Europe-Africa-Middle East) Clear PolyCarbonate, High Flow, UV Stabilization, Heat Stabilization |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® LUX1169 PC (Europe-Africa-Middle East) Lexan LUX1169 |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CX2244ME PC+ABS (Asia Pacific) Cycoloy* CX2244ME resin is a flame retardant PC/ABS blend featuring excellent balance of flow and impact together with UL-94 V0 rating at < 1mm. Cycoloy CX2244ME resin also demonstrates improved che.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL V03505 PPE+HIPS Noryl* V03505 is a 35% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KL004 is a compound based on Acetal Copolymer containing PTFE. Added features include Internally Lubricated. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® IQ325 PBT (Asia Pacific) PBT resin, using chemically recycled post consumer PET Bottles. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® X4850 PBT+PC (Europe-Africa-Middle East) Xenoy X4850 is a hydrostable, high modulus, high ductile PC/PBT blend. Furthermore, this resin provides high chemicalresistance, very low creep, low CTE, excellent fatique and high heat dimensional .. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50mm/min; ISO 527 |
Teijin Panlite® LS-2250 Friction and Abrasion Resistant Polycarbonate Resin It is compounded with fluorine powder to improve friction and abrasion resistance, meeting UL 94 V-2. The friction and abrasion resistance is superior than that of polyamidoacetal, maintaining excel.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP MFB82I PP (Europe-Africa-Middle East) LNP* Thermotuf* MFB82I is a compound based on Polypropylene resin containing Glass Fiber, Glass Bead. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL 731S PPE+HIPS (Europe-Africa-Middle East) NORYL 731S is an unfilled material, with a Vicat B/120 of 135C according ISO 306. NORYL 731S cust spec 1977 has been listed for potable water applications up to 85C by the UK WFBS according BS 6920 .. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-93 |
Wellman Wellamid® XT1573-N Impact Modified Nylon 66 Description: Impact Modified Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527; DIN 53455 |
Zell-Metall Engineering Plastics Zellamid 202 (PA 6) at 50% RH Zellamid® 202 is a tough material with high resistance to abrasion and impact. It features good mechanical properties. By water absorption the excellent shock and vibration resistance is increased... |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
Covestro Desmopan® DP 1490A Polyurethane Extrusion- and injection molding gradesuitable for extrusion blow moldinghigh melt stabilityvery large processing windowApplicationBellowsInjection molded engineering partsO-stringsHosesnon-reinforc.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® L 20 GM PA12 Product Description: Grilamid L 20 GM is a medium viscosity, heat stabilized polyamide 12 non-reinforced injection molding grade. This product has very good flow characteristics. Special features of.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® L 20 nat PA12 Medium viscosity unmodified Polyamide 12Information provided by EMS Grivory |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® L 25 H PA12 Product Description: Grilamid L 25 H is a high viscosity heat stabilized Polyamide 12 extrusion grade and is suitable for application requiring a long-term usage temperature of 100 - 120°C. The mai.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | Conditioned; ISO R 527 |
Addiplast Addinyl A2 1 Flame Retardant Nylon 66 Flame retardant, halogen freeInformation provided by Addiplast. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6600 GS 20 HWCP 20% Glass Sphere Filled Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 50.0 MPa @Temperature 23.0 °C |
7250 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 300ATB BK000 Acetal Homopolymer
(Unverified Data**) Delrin® 300ATB BK000 is a filled, medium viscosity, toughened acetal homopolymer for injection molding. It is well suited for antistatic applications.Information provided by DuPont Performance Poly.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-1,2 |
Qualchem Danamid FGFTALX2-5 20 Polyamide 6, 25% Glass Fiber Reinforced with glass fiber and minerals. Flame retardant, halogen-free (V-2)Information provided by Qualchem Zrt. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® X5630 PC+PET (Europe-Africa-Middle East) Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications |