Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 95.0 MPa | <= 13800 psi | ISO/R527 |
Polykemi AB POLYsan FL100 F20 SAN, Glass Fiber-Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 95.0 MPa | <= 13800 psi | ISO/R527 |
Polykemi AB SCANMID 6 B11^ FX25 FR10 Nylon 6, Glass Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | |
Radici Radiflam® A RV350AF (cond.) Nylon 66-35GF PA66 flame retardant injection molding grade with red phosphorus, halogen free. 35% Glass fiber reinforced, for items with high stiffness and good dimensional stability.Information provided by Radic.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Europe-Africa-Middle East) LNP* Konduit* RTF2B is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL34 PC LNP LUBRICOMP* DFL34 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
Gharda Chemicals GATONE™ 5600 PEEK, Low Viscosity Grade
(discontinued **) Low viscosity. grade for injection molding of thin sections & complex partsCHARACTERISTICS: Outstanding chemical resistance.Outstanding wear resistance.Outstanding resistance to hydrolysis.Excellen.. |
|||
Tensile Strength at Break | <= 95.0 MPa | <= 13800 psi | ISO/R527 |
Polykemi AB POLYfill PPH GF5040 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 LNP* KONDUIT* RTF2B is a compound based on Nylon 66 resin containing 10% Glass Fiber, 55% Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL34EH PC LNP* LUBRICOMP* DFL34EH is a compound based on Polycarbonate containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Easy Molding, Healthcare, Wear Resistant. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
DSM Akulon® K224-TPG3 Impact Modified Nylon 6-15% Glass Reinforced (European Grade) (Dry)
(discontinued **)&l The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | cond.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® BKV 130 GIT DUS008 900116 Nylon 6, Impact Modified PA 6, 30% glass fibers, injection molding, impact modified, GIT/WITInformation provided by LANXESS. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 10mm/min; ASTM D638 |
Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesExcellent size stabilityNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsE & E partsInforma.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
Lanxess Pocan® C 3230 XF 000000 PBT + PC, 30% Glass Fiber PBT+PC, 30% glass fibers, injection molding, improved flowability, low tendency to warp, improved surface finish |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 221 PA66, DRY Description TECHNYL ® A 221 is an unreinforced polyamide 66, medium viscosity, for injection molding, with a special crystallizing agent, for fast cycles. It is available in natural colors. Benef.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON Cycoloy_JK800 PC+ABS LNP* Stat-kon* Cycoloy_JK800 compound is an 8% carbon fiber reinforcedPC+ABS, electrostatic dissipative ECO conforming FR. Good hydrolytic stability. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 815F PBT+PET PBT+PET, 15% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp EB004 PEI LNP* Thermocomp* EB004 is a compound based on Polyetherimide resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF002SXS PA 66 LNP* THERMOCOMP* RF002SXS is a compound based on Nylon 66 resin contaning 10% Glass Fiber. Characteristcs of this grade are: Heat Stabilized. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend LNP THERMOCOMP* ZF406XXX is a compound based on PPO Blend resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP ZFM3314 PPE (Europe-Africa-Middle East) glas, mineral filled PPE |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PPX PPX640 PPE+PP 40% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | Vertical; ASTM D570 |
Unitika UNILATE® 1 SC PET Antistatic gradeUNILATE® products are plate materials prepared by using a polyethylene terephthalate (PET resin) as the main component, blending it with glass staple fiber, inorganic filler, and ot.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
Covestro Bayblend® T88 GF-10* Polycarbonate + SAN Glass Filled Impact Grade Developmental productInjection molding grade10 % GFoptimized heat ageing- and UV-stabilityvery good flowtensile modulus = 5100 MPaVicat/B 120 = 134 °CPreprocessingMax. Water content |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
DSM Arnite® TV4 230 SF PBT-15% Glass Reinforced (European and Asian Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® HR5315HF NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**)& 15% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate Crastin HR5315HF is a 15% glass reinforced PBT with high flow (HF) moderately toughened hydrolysis resistant (HR) resin. Excellen.. |
|||
Tensile Strength at Break | 95.0 MPa @Temperature -40.0 °C |
13800 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned) Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing c.. |
|||
Tensile Strength at Break | 95.0 MPa @Temperature -40.0 °C |
13800 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned) Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing c.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D638 |
BLUESTAR 101G20 PBT, 20% Glass Filled Typical Applications: Appliances, molded partsInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | STN EN ISO 527-2 |
Plastcom SLOVALEN PH 69 GF 30/1M Polypropylene reinforced with glass fiber Modified homopolymer PP for injection molding, reinforced with 30% glass fiber. Applied in all industry branches. Delivered in natural mode and in the full RAL color scale.Information Provided by Pl.. |