Polymer Property : Tensile Strength at Break = 9860 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Cycolac® INP576 ABS+SAN
Can be used as compounding additives for polymer blends. Medium molecular weight SAN. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direc..
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 104 PC
UL rated HB. 200 series recommended when V-2 rating required. 7.0 MFR, for thicker sections without sinks. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will..
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 104R PC
UL rated HB. 200 series recommended when V-2 rating required. 7.0 MFR, for thicker sections without sinks. Internal mold release. FDA food contact compliant in limited colors.Effective January 15..
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 121R PC
UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 17.5 MFR, for small, intricate parts. Internal mold release.
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 124R PC (Asia Pacific)
LEXAN 124R is a low viscosity multi purpose grade. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade is no longer supported with biocompatibility information an..
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 241 PC
General Purpose polycarbonate with 10.5 of melt flow rate. Improved flame retardance.
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 241S PC (Asia Pacific)
10.5 MFR. Improved flame retardance. Super mold release.
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 244R PC (Asia Pacific)
LEXAN 244R resin grade is a medium viscosity multi purpose product with improved flame resistance and release properties. It is also FDA food contact compliant available in limited colors.
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® FXE121R PC
Transparent PC. ILLUMINATE special effects (fluorescent/edge glow colors). MFR 18.2. Internal mold release.
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HP2C PC (Asia Pacific)
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains m..
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HP2NR PC (Europe-Africa-Middle East)
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no..
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HP6NR PC (Europe-Africa-Middle East)
Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no ..
Tensile Strength at Break 68.0 MPa
9860 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® HPH4704 PPC (Asia Pacific)
High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam steril..
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HPS2S PC (Asia Pacific)
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma steriliza..
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® IR2840 PC
7.0 MFR, for thicker sections without sinks. Internal mold release. FDA food contact compliant, natural only.Effective January 15th, 2007 this grade will no longer be supported with biocompatibilit..
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 141 PC
General purpose polycarbonate with melt flow rate of 10.5.
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 141 PC (Asia Pacific)
Nonhalogenated. 10.5 MFR.
Tensile Strength at Break 68.0 MPa
9860 psi
ISO 527
Nilit FRIANYL A63 TF-KV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass ball reinforced
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break 68.0 MPa
9860 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FXD9945A PC (Europe-Africa-Middle East)
UV stabilzed Visualfx FR PC with non-brominated and non-chlorinated flame retardant systems. It is available Only in white diffused effect(WH8B111X) meeting UL-94 V0 at 2mm for thin wall application..
Tensile Strength at Break 68.0 MPa
9860 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® HFD1413 PC Copolymer (Europe-Africa-Middle East)
11 MFR LEXAN High Flow Ductile Copolymer
Tensile Strength at Break 68.0 MPa
9860 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® HFD1433 PC Copolymer
11 MFR LEXAN High Flow Ductile Copolymer UV stabilized, available in transparent colors only
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HPS6R PC
Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). Contains a higher amount of mold release t..
Tensile Strength at Break 68.0 MPa
9860 psi
ISO 527
SABIC Innovative Plastics LNP COLORCOMP DX04401H PC
LNP* COLORCOMP* DX04401H is an unfilled Polycarbonate. Added feature of this grade is: Healthcare.
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl PKN4766 PPE+PS (Asia Pacific)
PPE+PS. Translucent. FDA compliant. High flow. Extrusion. Microwavable. Food packaging uses.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 68.0 MPa
9860 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66
LNP* LUBRICOMP* RI001 is a compound based on Nylon 66 resin containing 2% Silicone. Added feature of this grade is: Wear Resistant.
Tensile Strength at Break 68.0 MPa
9860 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6
LNP* STAT-LOY* PF303 is a Nylon 6 base resin containing 15% Glass Fiber. Added features of this grade includes: Antistat.
Tensile Strength at Break 68.0 MPa
9860 psi
5 mm/min; ISO 527
Eurostar Starpylen MX06050 PP, 30% Glass Filled, Injection Molded
Starpylen MX06050 is a 30% Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break 68.0 MPa
9860 psi
Plastcom SLOVAMID 6 LI LS PA6, improved strength, light stability
FeaturesPA 6 with the content of thermoplastic kaoutchouc. Impacted, for mouldings with high toughness either at minus temperatures, suitable for external use, eg. ski shoes, sports and safety helme..
Tensile Strength at Break 68.0 MPa
9860 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® HFD1433 PC Copolymer (Europe-Africa-Middle East)
11 MFR LEXAN High Flow Ductile Copolymer UV stabilized, available in transparent colors only
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® SFX123RU PC (Asia Pacific)
SFX123RU is a transparent SecurFX grade with improved flow, mold release and UV stabilizer. This grade is for security applications and contains proprietary authentication technology.This data was s..