Polymer Property : Charpy Impact Unnotched = 0.500 J/cm² Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Charpy Impact Unnotched 0.500 J/cm²

@Temperature -20.0 °C
2.38 ft-lb/in²

@Temperature -4.00 °F
Plastcom SLOVALEN PH 51 T 60 PP, 60% mineral filling
FeaturesModified homopolymer PP for injection moulding with the content of 60% microground, floated, chemically modified talc. General application in all industry. Delivered in natural mode and in t..
Charpy Impact Unnotched 0.500 J/cm²

@Thickness 102 mm,
Temperature -20.0 °C
2.38 ft-lb/in²

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
Premix Thermoplastics PRE-ELEC® PP 1394 Conductive Thermoplastic Compound
PRE-ELEC® PP 1394 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E..
Charpy Impact Unnotched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/2C
SABIC Innovative Plastics Lexan® 1278R PC (Europe-Africa-Middle East)
LEXAN 1278R is a medium viscosity, 20% glass reinforced, flame retardant grade, offering a very high rigidity. It is especially designed for applications like industrial enclosures and fuse boxes re..
Charpy Impact Unnotched 0.500 - 1.00 J/cm²

@Temperature 23.0 °C
2.38 - 4.76 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/1eA
Raschig Group 2567 AMC
Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and ..
Charpy Impact Unnotched 0.500 - 1.00 J/cm²

@Temperature 23.0 °C
2.38 - 4.76 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
Raschig Group 2568 AMC
Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s..
Charpy Impact Unnotched 0.500 - 1.00 J/cm²

@Temperature 23.0 °C
2.38 - 4.76 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
Raschig Group 5553 DAP
Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Charpy Impact Unnotched 0.500 - 0.700 J/cm²

@Temperature 23.0 °C
2.38 - 3.33 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
Raschig Group MELOPLAS® 150 MF
Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr..
Charpy Impact Unnotched 0.500 - 0.900 J/cm²

@Temperature 23.0 °C
2.38 - 4.28 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
Raschig Group MELOPLAS® 152 MF
Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Charpy Impact Unnotched 0.500 - 0.900 J/cm²

@Temperature 23.0 °C
2.38 - 4.28 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
Raschig Group MELOPLAS® 181 MF
Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc..
Charpy Impact Unnotched 0.500 - 0.800 J/cm²

@Temperature 23.0 °C
2.38 - 3.81 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
Raschig Group MELOPLAS® 182 MF
Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf..
Charpy Impact Unnotched 0.500 - 0.800 J/cm²

@Temperature 23.0 °C
2.38 - 3.81 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
Raschig Group MELOPLAS® 183 MF
Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18..
Charpy Impact Unnotched 0.500 - 1.00 J/cm²

@Temperature 23.0 °C
2.38 - 4.76 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
Raschig Group RALUPOL® 4385 UP
Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy..
Charpy Impact Unnotched 0.500 - 1.00 J/cm²

@Temperature 23.0 °C
2.38 - 4.76 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
Raschig Group RALUPOL® 4806 UP
Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80..
Charpy Impact Unnotched 0.500 - 1.00 J/cm²

@Temperature 23.0 °C
2.38 - 4.76 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179 1eU
Raschig Group SURAPLAST 54 UPA
Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..