- Polymer Property : Tensile Strength, Yield = 123000 psi
Polymer Property : Tensile Strength, Yield = 123000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 850 MPa @Temperature 400 °C |
123000 psi @Temperature 752 °F |
|
| International Mold Steel DH2F Pre-Hardened H13-Type Mold Steel Description: DH2F is one of the best machining pre-hardened H13-type steels available.Unique Characteristics: 38-42 HRc hardness.Through hardened for exceptional dimensional stability.Cuts mold maki.. |
|||
| Tensile Strength, Yield | 850 MPa @Strain 0.200 % |
123000 psi @Strain 0.200 % |
Typical, Longitudinal Direction |
| Industeel CLC 1.2312 Prehardened Mold Steel (300HB/32HRC) with Improved Machinability Description: CLC 1.2312 is a chromium-manganese-molybdenum grade designed for plastic mold industry. This grade is normally delivered in a prehardened condition at a hardness level of 300HB/32HRC. T.. |
|||
| Tensile Strength, Yield | 847 MPa @Strain 0.200 %, Temperature 649 °C |
123000 psi @Strain 0.200 %, Temperature 1200 °F |
|
| Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Tensile Strength, Yield | 850 MPa @Strain 0.200 %, Temperature 50.0 °C |
123000 psi @Strain 0.200 %, Temperature 122 °F |
|
| Special Metals UDIMET® alloy 520 Superalloy UDIMET® alloy 520 is a precipitation-hardenable nickel base superalloy with an exceptional combination of high-temperature mechanical properties, corrosion resistance and forgeability characteris.. |
|||
| Tensile Strength, Yield | 850 MPa @Strain 0.200 %, Temperature 400 °C |
123000 psi @Strain 0.200 %, Temperature 752 °F |
|
| Special Metals UDIMET® alloy 520 Superalloy UDIMET® alloy 520 is a precipitation-hardenable nickel base superalloy with an exceptional combination of high-temperature mechanical properties, corrosion resistance and forgeability characteris.. |
|||
| Tensile Strength, Yield | 850 MPa @Strain 0.200 % |
123000 psi @Strain 0.200 % |
20% Reduction of Section |
| Schmolz + Bickenbach LeanDupâ„¢ 35N Stainless Steel Bar Description: LeanDupâ„¢ 35N also known as (Uranus 35 N) is a dual phase austentic-ferritic stainless steel that has the ability to become as important as 316L. It offers better corrosion resistan.. |
|||
| Tensile Strength, Yield | 848 MPa @Temperature 24.0 °C |
123000 psi @Temperature 75.2 °F |
|
| Hexcel® HexPly® F155 Epoxy Resin, W3T282 Carbon Fabric Hexcel designation: W3T282-42"-F155; Fiber: T300 Toho®Information provided by HexCel |
|||