Polymer Property : Tensile Strength, Yield = 641 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	641 MPa @Thickness 12.7 mm, Temperature 20.0 Â°C	93000 psi @Thickness 0.500 in, Temperature 68.0 Â°F	0.2% offset
Haynes UltimetÂ® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Yield	641 MPa @Strain 2.00 %, Temperature 538 °C	93000 psi @Strain 2.00 %, Temperature 1000 °F	H1150
Crucible Steel 15-5 Precipitation Hardening Stainless Steel Crucible 15-5 is a Premium Quality precipitation-hardening stainless steel which is capable of high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is a V..
Tensile Strength, Yield	641 MPa @Strain 2.00 %, Temperature 538 °C	93000 psi @Strain 2.00 %, Temperature 1000 °F	H1150
Crucible Steel 17Cr-4Ni Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a precipitation-hardening stainless steel which is capable of a high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is martensitic a..
Tensile Strength, Yield	641 MPa @Strain 2.00 %, Temperature 538 °C	93000 psi @Strain 2.00 %, Temperature 1000 °F	H1150
Crucible Steel 17Cr-4Ni Super-X® Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a version of 17CR-4Ni which has been modified to substantially improve machinability and other properties. Patented 17Cr-4Ni Super-X meets industry specifications for 17Cr-4Ni. ..
Tensile Strength, Yield	641 MPa @Temperature 149 °C	93000 psi @Temperature 300 °F	Cold Worked
ATI Wah Chang TI-3Al-2.5V Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working an..