Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | Orientation not specified; ASTM D882 |
DuPont™ Kapton® 50HN Polyimide Film, 13 Micron Thickness Film thickness 13 micron (0.5 mil)All purpose polyimide film. Can be laminated, diecut, slit, formed, or adhesive-coated. Available in thicknesses from 0.3 mil (7.5 µm) to 5 mil (125 µm).General.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 378 Polyester Film Melinex® 378 is a translucent, matte, polyester film which has a rougher surface (lower surface gloss) than Melinex® 377.Approvals: UL Recognition - Product has been registered with Underwriters L.. |
|||
Film Tensile Strength at Break, MD | >= 172 MPa | >= 25000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 473 Polyester Film, 200 Gauge Melinex® 473 is a high clarity polyester film manufactured with a coating on one surface that improves slip and handling characteristics. The opposite surface is raw polyester (non-coated). The sli.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 515 Polyester Film A high clarity film which is two side pretreated for slip to combine good handling properties with high clarity and brilliance.Typical Applications: MELINEX® 515 is suitable for applications which .. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 623 Polyester Film, 750 Gauge Melinex® 623 is a super clear polyester film pretreated on both surfaces to give superior solvent adhesion and improved handleability.Information provided by DuPont. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Melinex® WCW Polyester Film, 75 Gauge Melinex® WCW is a translucent white polyester film with a rough surface for superior handling characteristics.Information provided by DuPont. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® HS Polyester Film, 48 Gauge (12 µm) Data provided by DuPont Packaging Polymers.An uncoated, transparent polyester packaging film designed for heat shrink applications. It is currently available in 48, 65, 80, and 150 gauges, and othe.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® M34 Polyester Film, 75 Gauge (20 µm), PVDC Coated Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, solvent coated on one side with a PVDC copolymer. The coating is heat sealable, and is an excellent moisture and o.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Mylar® M461 Polyester Film, 60 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® MC2 Polyester Film, 100 Gauge (25 µm), PVDC Coated Data provided by DuPont Packaging Polymers.A polyester film with a vacuum deposited layer of aluminum on one side and overcoated on both sides with a heat sealable PVDC copolymer. The film has exce.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB01 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB01 (formerly known as XM924) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and a polyvinylidene chlor.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB12AF Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the op.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL12 (formerly known as XM963A) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sea.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL12 (formerly known as XM963A) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sea.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® OL13 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL13 (formerly known as XM110) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat seal.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RB43 Polyester Film, 100 Gauge Mylar® RB43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer on one side and a polyvinylidene chloride (PVdC) layer on the opposite side. Mylar® R.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL32 (formerly known as XM999) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL32 (formerly known as XM999) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL32 (formerly known as XM999) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL32 (formerly known as XM999) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL33 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL33 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL4 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL4 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film .. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 24900 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. Mylar® RL43 is designed to produce stro.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 140 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 48 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 500 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Mylar® M461 Polyester Film, 400 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil.. |
|||
Film Tensile Strength at Break, MD | 172 MPa | 25000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 200 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |