Polymer Property : Film Tensile Strength at Break, MD = 22000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329 Polyester Film, 1000 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329 Polyester Film, 1400 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329 Polyester Film, 142 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329 Polyester Film, 300 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329 Polyester Film, 380 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329 Polyester Film, 500 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329 Polyester Film, 700 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329 Polyester Film, 75 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329 Polyester Film, 820 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329S Polyester Film, 92 Gauge An opaque white film with good handling properties, a unique glossy appearance, and a lower shrinkage for special applicationsInformation provided by DuPont.
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 329W Polyester Film, 300 Gauge An opaque white film with good handling properties and a unique glossy appearance. 329W has same properties as 329 with the only exception being it is wound reverse. See the 329 datasheet for detail..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 339 Polyester Film, 1000 Gauge Melinex® 339 is an opaque white polyester film with good handling properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings.Typical Applications: Melinex® 339..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 339 Polyester Film, 380 Gauge Melinex® 339 is an opaque white polyester film with good handling properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings.Typical Applications: Melinex® 339..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 339 Polyester Film, 820 Gauge Melinex® 339 is an opaque white polyester film with good handling properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings.Typical Applications: Melinex® 339..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 547 Polyester Film, 400 Gauge Information provided by DuPont.
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® C Polyester Film, 10 Gauge Mylar® Type C films are available in a wide range of generally thinner gauges (typically 10 through 92) that offer excellent electrical properties, combined with superior strength and dimensional s..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 1000 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 400 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 500 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 700 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® P25 Polyester Film, 50 Gauge Product Description: Mylar® P25 is an uncoated, transparent polyester packaging film designed to be combined with a sealant layer, where the resulting structure will be shallow draw thermoformed. S..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® P25 Polyester Film, 75 Gauge Product Description: Mylar® P25 is an uncoated, transparent polyester packaging film designed to be combined with a sealant layer, where the resulting structure will be shallow draw thermoformed. S..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® P25T Polyester Film, 75 Gauge Product Description: Mylar® P25T is a transparent polyester packaging film designed to be combined with a sealant layer, where the resulting structure will be shallow draw thermoformed. It has a co..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® TL Polyester Film Mylar® Type TL film is a film specified for card protection engineered to provide an identical shrinkage between MD/TD and also possessing good properties of resistance to moisture, oils and chemic..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® 339 Polyester Film, 500 Gauge Melinex® 339 is an opaque white polyester film with good handling properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings.Typical Applications: Melinex® 339..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® AF Polyester Film Melinex® AF is a clear polyester film coated both sides with an anti-fog coating. Typical Applications: Typical applications include face shields, masks, visors, and other industrial uses.Informati..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Melinex® WLB Polyester Film, 500 Gauge Melinex® WLB is a polyester film with a white surface, a light grey surface and very high opacity. General Product Info: Melinex® WLB offers a film with a white surface and very high opacity. It c..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 92 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, MD	152 MPa	22000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 300 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, MD	152 - 186 MPa	22000 - 27000 psi	Average value: 172 MPa Grade Count:10
Overview of materials for Polyvinyl Dichloride (PVDC) Coated Polyester Film This property data is a summary of similar materials in the MatWeb database for the category "Polyvinyl Dichloride (PVDC) Coated Polyester Film". Each property range of values reported is minimum an..