Polymer Property : Film Tensile Strength at Break, MD = 3600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
MD-TD Average; ASTM D882
DuPont Elvax® 3121A Ethylene-Vinyl Acetate Copolymer Resin for Blown Film  (discontinued **)
7.5 wt% Vinyl Acetate.General Elvax® information: Elvax® packaging grade resins include low seal temperatures for use in coextrusions or for packaging temperature sensitive materials, excellent dr..
Film Tensile Strength at Break, MD 24.8 - 76.5 MPa
3600 - 11100 psi
Average value: 47.5 MPa Grade Count:18
Overview of materials for Medium Density Polyethylene (MDPE), Film Grade
This property data is a summary of similar materials in the MatWeb database for the category "Medium Density Polyethylene (MDPE), Film Grade". Each property range of values reported is minimum and m..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
LyondellBasell Petrothene® NA271009 Medium Density Polyethylene
ApplicationsPETROTHENE NA 271-009 is a medium density polyethylene resin designed to overwrap film applications. NA 271-009 exhibits good film optics and high stiffness. Regulatory StatusNA 271-009..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
LyondellBasell Petrothene® NA442051 Low Density Polyethylene
ApplicationsPETROTHENE NA 442 is a series of low density/EVA copolymer resins for high impact/high clarity packaging and lamination applications. NA 442 exhibits excellent processability and good b..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
LyondellBasell Petrothene® NA951000 Low Density Polyethylene
ApplicationsPETROTHENE NA 951 is a series of homopolymer resins specially designed for industrial and consumer packaging and liner and bag applications. NA 951 has an excellent balance of processab..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
LyondellBasell Petrothene® NA967000 Low Density Polyethylene, Film Extrusion Grade
Petrothene NA967000 is a low density polyethylene resin designed for blown film, general purpose and industrial packaging applications. NA967000 exhibits good processing characteristics and impact s..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
D638
Westlake EF528 18.5% Ethylene Vinyl Acetate Copolymer
Westlake ELEVATE™ EF528 is an ethylene vinyl acetate copolymer with 18.5% VA. EF528 is designed for blown and cast films requiring excellent optics and low heat seal initiation. High melt strength ..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D638
Westlake Elevate™ DA528AA 18.5% Ethylene Vinyl Acetate Copolymer
Westlake ELEVATE™ DA528 is an ethylene vinyl acetate copolymer with 18.5% VA. DA528 is designed for blown and cast films requiring excellent optics and low heat seal initiation. High melt strength..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
Westlake Elevate™ DA528AA Ethylene Vinyl Acetate Copolymer
Developmental ProductDescription: Westlake ELEVATE™ DA528 is an ethylene vinyl acetate copolymer with 18.5% VA. DA528 is designed for blown and cast films requiring excellent optics and low heat s..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
D638
Westlake ELEVATE™ EF529 18.5% Ethylene Vinyl Acetate Copolymer
Westlake ELEVATE™ EF529 is an ethylene vinyl acetate copolymer with 18.5% VA. It contains no slip or antiblock and is designed for blown and cast films requiring excellent optics and low heat seal ..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil Escorene™ FL 00309 Ethylene Vinyl Acetate Copolymer (European Grade)
Product Description: FL 00309 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 270°C (513°F) may cause resin degradation. Availability: Africa & M..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil HDPE HD 7925.30 High Density Polyethylene Resin
Product Description: HD 7925.30 is a medium molecular weight HDPE homopolymer for use in blown and cast film applications. Typical applications include those with low WVTR and clarity requirements.A..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil LD 117.85 Blown Overwrap Film Resin
Product Description: LD 117.85 is a homopolymer film resin with good clarity and excellent stiffness. Film made from LD 117.85 resin can be used in overwrap applications and in push-through type pac..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil LDPE LD 100.BW Low Density Polyethylene Resin
Product Description: LD 100.BW is a LDPE grade, offering a good balance of optical and mechanical properties. Several additive packages are available according to the required surface properties.Ava..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil LDPE LD 100AC Low Density Polyethylene Resin
Product Description: LD 100 series are LDPE grades, offering a good balance of optical and mechanical properties. Several additive packages are available according to the required surface properties..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil LDPE LD 100BR Low Density Polyethylene Resin
Product Description: LD 100 series are LDPE grades, offering a good balance of optical and mechanical properties. Several additive packages are available according to the required surface properties..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil LDPE LD 100BW Low Density Polyethylene Resin
Product Description: LD 100 series are LDPE grades, offering a good balance of optical and mechanical properties. Several additive packages are available according to the required surface properties..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil LDPE LD 105.30 Low Density Polyethylene Resin
Product Description: LD 105 resins are homopolymer packaging film resins designed for applications requiring outstanding clarity with good stiffness. These resins can be processed in either blown or..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil LDPE LD 105.BR Low Density Polyethylene Resin
Product Description: LD 105 resins are homopolymer packaging film resins designed for applications requiring outstanding clarity with good stiffness. These resins can be processed in either blown or..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
ExxonMobil LDPE LD 117.85 Low Density Polyethylene Resin
Product Description: LD 117.85 is a homopolymer film resin with good clarity and excellent stiffness. Film made from LD 117.85 resin can be used in overwrap applications and in push-through type pac..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
Dow INTEGRAL™ 899A Monolayer Adhesive Film
INTEGRAL 899A Adhesive Film is a versatile heat-activated film that bonds to such substrates as: Polyethylene, Nylon, Polyester, Fiberglass, Glass, Polyurethane Foams/Sheet, Acrylic Adhesives, Wood..
Film Tensile Strength at Break, MD 24.8 MPa

@Thickness 0.0356 mm
3600 psi

@Thickness 0.00140 in
ASTM D-882
Bapolene® 270F Low Density Polyethylene Film Extrusion Resin
Bapolene® 270F is an LDPE for blown film requiring superior clarity. It contains 1600 ppm antiblock and 725 ppm slip additives. This product meets the Food and Drug Administration requirements of ..
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
MD-TD Average; ASTM D882
DuPont Elvax® 3128 Ethylene-Vinyl Acetate Copolymer Resin for Blown Film  (discontinued **)
8.9 wt% Vinyl Acetate.Elvax® 3128 is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resin..