Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | 50 µm (2 mil) film; ASTM D882 |
DuPont Nucrel® 30707SR Ethylene-Acrylic Acid Copolymer Resin for Film and Extrusion Coating
(discontinued **) 7 wt% Acrylic Acid.Nucrel® 30707SR is an ethylene-acrylic acid copolymer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusio.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
LyondellBasell Petrothene® NA340141 Low Density Polyethylene ApplicationsPETROTHENE NA 340 is a LDPE/EVA copolymer resin designed for quality bags and special film applications requiring clarity and excellent impact strength. Typical applications include hea.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
LyondellBasell Petrothene® NA340163 Low Density Polyethylene ApplicationsPETROTHENE NA 340 is a LDPE/EVA copolymer resin designed for quality bags and special film applications requiring clarity and excellent impact strength. Typical applications include hea.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
LyondellBasell Petrothene® NA340185 Low Density Polyethylene, Film Extrusion Grade PETROTHENE NA340 is a series of LDPE/EVA copolymer resins designed for quality bags and special film applications that require clarity and excellent impact strength. Typical applications include hea.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
LyondellBasell Petrothene® NA340212 Low Density Polyethylene, Film Extrusion Grade PETROTHENE NA340 is a series of LDPE/EVA copolymer resins designed for quality bags and special film applications that require clarity and excellent impact strength. Typical applications include hea.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | 500mm/min, Ultimate; ASTM D638 |
LG Chemical SEETEC BF415 LDPE Characteristics: Good Processability and Excellent Optical Properties Applications: Masking filmCAS No. 9002-88-4Information provided by LG Chemical |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | 500mm/min, Ultimate; ASTM D638 |
LG Chemical SEETEC BF500 LDPE Characteristics: Good Processability and Good Optical Properties Additives: Antiblocking Agent, Slip AgentApplications: Industrial Film & Food PackageCAS No. 9002-88-4Information provided by LG Chem.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
LyondellBasell Petrothene® NA340013 Low Density Polyethylene ApplicationsPETROTHENE NA 340 is a LDPE/EVA copolymer resin designed for quality bags and special film applications requiring clarity and excellent impact strength. Typical applications include hea.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | MD-TD Average; ASTM D882 |
DuPont Elvax® 3130 Ethylene-Vinyl Acetate Copolymer Resin for Blown Film 12 wt% Vinyl Acetate.General Elvax® information: Elvax® packaging grade resins include low seal temperatures for use in coextrusions or for packaging temperature sensitive materials, excellent dra.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | 50 µm (2 mil) film; ASTM D882 |
DuPont Nucrel® 30707 Ethylene-Acrylic Acid Copolymer Resin for Film and Extrusion Coating 7 wt% Acrylic Acid.Nucrel® 30707 is an ethylene-acrylic acid copolymer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion .. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
ExxonMobil LD 051.LQ Shrink Film Resin L Product Description: LD 051.LQ blown film resin is a fractional melt index grade designed for demanding heavy duty film applications, and combines excellent strength properties with outstanding pr.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
ExxonMobil LD 071.LQ Blown Film Resin L Product Description: LD 071 Series case wrap film resins combine good processability with excellent strength and good film optics for bundling applications requiring proper shrink performance, tou.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
ExxonMobil LD 071.LR Blown Film Resin Product Description: LD 071 Series case wrap film resins combine good processability with excellent strength and good film optics for bundling applications requiring proper shrink performance, tough.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
ExxonMobil LDPE LD 051.LQ Low Density Polyethylene Resin Product Description: LD 051.LQ blown film resin is a fractional melt index grade designed for demanding heavy duty film applications, and combines excellent strength properties with outstanding proc.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
ExxonMobil LDPE LD 071.LQ Low Density Polyethylene Resin Product Description: LD 071 Series case wrap film resins combine good processability with excellent strength and good film optics for bundling applications requiring proper shrink performance, tough.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
ExxonMobil LDPE LD 071.LR Low Density Polyethylene Resin Product Description: LD 071 Series case wrap film resins combine good processability with excellent strength and good film optics for bundling applications requiring proper shrink performance, tough.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
ExxonMobil LDPE LD 136.MN Low Density Polyethylene Resin Product Description: LD 136.MN is a homopolymer film resin with good clarity. The resin is suitable for processing on blown film equipmentAvailability: Latin America, North America and South America.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
Dow INTEGRAL™ 906 Multilayer Adhesive Film INTEGRAL 906 Adhesive Film is a heat-activated, thermally stable adhesive film capable of bonding to urethane foam-baked fabrics, polyester and nylon fabrics, fiberglass, and rigid urethanes.Informa.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
Dow INTEGRAL™ 909 Monolayer Adhesive Film / Automotive Headliners INTEGRAL 909 Adhesive Film is a versatile heat-activated film that bonds to such substrates as: Polyethylene, Nylon, Polyester, Fiberglass, Polyurethane Foams, Wood, Paperboard, Cotton, Non-wovens,.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
Dow INTEGRAL™ 917 Monolayer Bonding Film INTEGRAL 917 Adhesive Film is a single layer adhesive film for use where a higher flow rate and lower melt point are required. It is useful for bonding heat sensitive materials, or for porous subst.. |
|||
Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
Formosa Plastics Formolene® L62005E2T1 Film (Hexene Grade) LLDPE
(discontinued **) Hexene Copolymer (High slip and antiblock, with processing aid)Applications: Blown film, high strength applicationsBlown film, high strength applicationsMeets all requirements of the U.S. Food and D.. |
|||
Film Tensile Strength at Break, MD | 25.5 - 74.5 MPa | 3700 - 10800 psi | Average value: 44.0 MPa Grade Count:80 |
Overview of materials for Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade". Each property range of values reported is m.. |