Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
Polimeri Europa Flexirene® FH 56 A Butene Copolymer Linear Low Density Polyethylene Flexirene FH 56 A is a butene copolymer with medium density (C4-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films manufactured with Flexirene FH 56 A are characte.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
Polimeri Europa Clearflex® FG B0 Very Low Density Polyethylene Clearflex FG B0 is a linear low density polyethylene, with antioxidants, suitable for blown film technology.Films made with Clearflex FG B0 are highly transparent, have good sealing properties, even.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
Polimeri Europa Clearflex® H&T LGH 138 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T LGH 138 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, slip agent, antiblocking and processing aid, suitable for blown film extrusion.Films obtai.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Chevron Phillips 7109BKT LLDPE Blown Film Resin, Hexene Copolymer
(discontinued **) Resin Type: Hexene Copolymer, Medium Slip, Medium Antiblock Version of 7109TCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Low COF, Can be used straight or blended with LDPE or HDPE... |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527 |
Total Finathene® LL 4010 FE 18 LLDPE film
(discontinued **) Linear low density polyethylene made by gas phase process for blown film applications. Advised temperature profile: 190 to 220°C.Information provided provided by Total Petrochemicals.Total Petroche.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527 |
Total Finathene® LL 4010 FH 18 LLDPE film
(discontinued **) Linear low density polyethylene made by gas phase process for blown film applications. Advised temperature profile: 190 to 220°C.Information provided provided by Total Petrochemicals.Total Petroche.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
ExxonMobil Escorene® LD-103 LDPE Industrial Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer industrial film resin with excellent toughness. LD-103 has a low melt index which gives excellent impact strength and melt strength o.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
NOVA Chemicals Sclair® 16A Butene HDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, good barrier properties.Applications: Merchandising bags, lamination, co-extrusion.Data provided by the manufacturer. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
LyondellBasell Petrothene® GA501021 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 501series of resins are pelletized linear low density polyethylene for film extrusion applications requiring excellent drawdown and toughness. These resins have excellent .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
LyondellBasell Petrothene® GA501022 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 501series of resins are pelletized linear low density polyethylene for film extrusion applications requiring excellent drawdown and toughness. These resins have excellent .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
LyondellBasell Petrothene® GA501023 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 501series of resins are pelletized linear low density polyethylene for film extrusion applications requiring excellent drawdown and toughness. These resins have excellent .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Iran Petrochemical (PCC) LL 18XF5 N Linear Low Density Polyethylene LL 18XF5 N is a terpolymer of ethylene, propylene and butene-1 for high film strength applications, especially heavy duty shipping sacks, ice bags, frozen food bags, potato bags, and agriculture fil.. |
|||
Film Tensile Strength at Break, MD | 40.0 - 60.0 MPa | 5800 - 8700 psi | ISO 527-3 |
Borealis BB213CF Polypropylene Copolymer BB213CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: BB213CF is recommended for food packaging.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | |
UBE 5033FDX27 Air Blown Nylon 6/66 Film Specialties: High slip typeMedium shrinkApplications: General purposeSuitable for Water cooling processProcessing: Sausage casings (Water)Big bag (Air blown)Information provided by UBE. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
Borealis Bormed™ RD804CF Polypropylene Random Copolymer Bormed™ RD804CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications Bormed™ RD804CF is recommended for packaging for med.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Total PPH M3661 Metallocene Isostatic Polypropylene Polymer, Cast Film Extrusion TOTAL Petrochemicals Polypropylene M3661 is an isostatic form of homopolymer made via TOTAL proprietary metallocene catalyst technologyRecommended Applications. M3661 is a medium molecular weight m.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem BF 0323 HC LDPE Blown Film Extrusion Polyethylene Description: BF0323HC is a high molecular weight grade produced under high pressure. Films obtained with this product show excellent mechanical and optical properties38µm film gauge, obtained in 75.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
Braskem GM9450F HDPE Blown Film Extrusion Polyethylene HDPE GM9450F is a high-density polyethylene developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and e.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem Green PE SLH118 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLH118 is a Linear Low Density Polyethylene, copolymer of hexene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good process.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem Green PE SLH218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLH218 is a LLDPE Hexene copolymer produced by Braskem. It shows a good balance between optical properties, mechanical properties (Mainly stretchability), sealability and processability.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem LHB 118/21 AF LLDPE Blown Film Extrusion Polyethylene Description: LHB118/21 AF is a LLDPE copolymer produced by Braskem. It is a ready-to-use product since it contains 10% LDPE. Its additive package was optimized to avoid blocking, even at low thickne.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem LL118/21 Blown Film Extrusion Linear Low Density Polyethylene Description: LL118/21 is a LLDPE Butene copolymer produced by Braskem. It is a general purpose product that shows a good processing performance balanced with good optical and mechanical properties a.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem LL218 Cast Film Extrusion Linear Low Density Polyethylene Stretch films; Liners; LDPE and HDPE blends; Packages for general use.Information provided by Braskem. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
Braskem LL6800N LLDPE Blown Film Extrusion Polyethylene Copolymer LL6800N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains antiblock, proc.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
Braskem LL6802N LLDPE Blown Film Extrusion Polyethylene Copolymer LL6802N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing aid .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
Braskem LL6901S LLDPE Blown Film Extrusion Polyethylene Copolymer LL6901S is a LLDPE Butene copolymer produced by Braskem. It is a ready to use product since it's been compounded with 15% LDPE. It is a general purpose product that shows a good processing performan.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
ExxonMobil Exceed™ 2227ED Metallocene Polyethylene Resin (European Grade) Product Description: Exceed 2227ED is a metallocene ethylene-hexene copolymer. It offers an excellent balance of high modulus and impact strength. The higher melt index makes it ideally suited for L.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
ExxonMobil Exceed™ 2018EB Blown Film Resin
(discontinued **) Exceed 2018EB resin is an ethylene based polymer produced with metallocene single site catalysts using ExxonMobil Chemicals Exxpol® Technology. The higher melt index makes this polymer ideally sui.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
NOVA Chemicals Sclair® 14J1 Octene LMDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, good clarity, high strength and toughness.Applications: Produce film.Data provided by the manufacturer. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem LF0720/20AF Blown Film Extrusion Linear Low Density Polyethylene Description: LF0720/21AF is a LLDPE Butene copolymer produced using Unipol process technology. It shows excellent optical properties associated with good balance of mechanical properties, processing.. |