Polymer Property : Tensile Strength, Yield = 123000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 850 - 1050 MPa
123000 - 152000 psi
Swaged after Sintering
MarkeTech 95-3-2 Tungsten Alloy, AMS-T-21014 Class 3
Used to fabricate parts to near net size and several processes to produce high quality tungsten based materials.Tungsten heavy alloys have very high melting point and have a density twice that of st..
Tensile Strength, Yield 845 MPa

@Strain 0.200 %
123000 psi

@Strain 0.200 %
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction
Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit..
Tensile Strength, Yield 845 MPa

@Strain 0.200 %
123000 psi

@Strain 0.200 %
Haynes 242® alloy, bar and rings, annealed and aged
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Tensile Strength, Yield 845 MPa

@Strain 0.200 %
123000 psi

@Strain 0.200 %
Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F)
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Yield 850 MPa

@Strain 0.200 %
123000 psi

@Strain 0.200 %
Precipitation Hardened. Value at room temperature
Special Metals INCONEL® Alloy X-750
A nickel-chromium alloy similar to INCONEL alloy 600 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good resistance to corrosion and oxidation along with hig..
Tensile Strength, Yield 850 MPa

@Strain 0.200 %
123000 psi

@Strain 0.200 %
Precipitation Hardened. Value at room temperature
Special Metals NIMONIC® Alloy 115
A precipitation-hardenable nickel-chromium-cobalt alloy with an addition of molybdenum for solid-solution strengthening. It is similar to NIMONIC alloy 105 but has higher levels of aluminum and tit..
Tensile Strength, Yield >= 850 MPa
>= 123000 psi
After bake hardening
SSAB Tunnplat Docol® 1000 DP High-strength Steel
High-strength SteelCharacteristics: The steels are annealed at temperatures between 750°C and 850°C, depending on the grade of steel, and then are hardened by quenching in water. Tempering is..
Tensile Strength, Yield >= 850 MPa
>= 123000 psi
80<x=100mm
ThyssenKrupp XABO® 960 Structural Steel
This Material Specification applies to liquid-quenched and tempered heavy plates from 3 up to 100 mm in thickness, made of the high-strength special structural steels XABO® 890 and XABO® 960.Appli..
Tensile Strength, Yield 850 MPa
123000 psi
90º, RT, Dry; EN2561
Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 50%/G939 HS Carbon
Information provided by HexCel
Tensile Strength, Yield 848 MPa

@Strain 0.200 %
123000 psi

@Strain 0.200 %
Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 52% Cold Worked
Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Vacuum arc remelted (VAR), low carbon version of Type 316 stainless. The secondary premium melting step (VAR) imparts impro..
Tensile Strength, Yield 848 MPa

@Strain 0.200 %
123000 psi

@Strain 0.200 %
Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1121°C 1 hr
Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h..
Tensile Strength, Yield 845 MPa
123000 psi
Hardened 1800°F, Tempered 900°F
ATI Allegheny Ludlum 410 Martensitic Stainless Steel
Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for..
Tensile Strength, Yield 850 MPa

@Strain 0.200 %
123000 psi

@Strain 0.200 %
Haynes 25 alloy, room temperature after 10% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Tensile Strength, Yield 845 MPa

@Strain 0.200 %
123000 psi

@Strain 0.200 %
typical
ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 482°C Temper
Allegheny Ludlum Type 410 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainles..