Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D412 |
Polymax® Maxelast® F02-138A TPE, Halogen Free Extrusion Grade Characteristics: Good melt strengthSoft touchSmooth surface with dry feelGood weather and heat resistanceWide range of hardnessEasy processing Halogen FreeLow smoke emissionRoHs compliantDesigned to.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
SABIC 324CN Linear Low Density Polyethylene for Wire & Cable Product Description: 324CN is a Linear Low Density Polyethylene natural resin for wire and cable applications. It contains a low level of antioxidants and does not contain any slip or antiblock a.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ISO 527 |
Polimeri Europa Riblene® GM 30 R Low Density Polyethylene - Coating Grade Riblene GM 30 R is a medium fluidity low density polyethylene resin (LDPE).Main Applications: Riblene GM 30 R is suitable for coating applications where low neck-in and high manufacturing speed are.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML7672 PC (Asia Pacific) Non FR PC + GF, UV-Stabilizer, balanced flow & impact. Available in Opaque only. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
Chevron Phillips 1006 LDPE Injection Molding Resin
(discontinued **) Resin Type: homopolymerCharacteristics: excellent flexibility, excellent flow, good warping resistance, moderate mold release, moderate ESCRApplications: large housewares, tamper evident snap-on cap.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
Huntsman PE1033 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Good opticals, impact strength, good processing properties, and stiffnessApplications: Film extrusion: general purpose packaging and film applications.FDA No.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
Huntsman PE1037 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Medium clarity packaging film and good draw down characteristics.Applications: Film extrusion: general purpose packaging and film applications.FDA Notes: Con.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | |
LyondellBasell Lupolen® 2420 F LDPE Film, blow moldings.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | |
LyondellBasell Lupolen® 2420 K LDPE, Film Grade FilmData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | |
LyondellBasell Lupolen® 2425 K LDPE, Film Grade FilmData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
Tensile Strength, Yield | >= 11.0 MPa | >= 1600 psi | |
Kazanorgsintez M 168 Polymer Composition for Rotary Molding Production Method: Composition is produced on the basis of 11503-070 grade low density polyethylene and 276-03 grade high density polyethylene composition. Application: Compositions are designed.. |
|||
Tensile Strength, Yield | 11.0 MPa @Strain 0.200 %, Temperature 1204 °C |
1600 psi @Strain 0.200 %, Temperature 2199 °F |
|
Haynes HR-160® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | Elastic; ASTM D412 |
Multibase Multi-Flex® A 8502 LC UV RXF/YYWA Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D412 |
Teknor Apex Flexalloy® 3501-50-NT Polyvinyl Chloride Elastomer Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Features: Ultra High MW, Ethylene Oxide SterilizableForms-PelletsProcessing-Extrusion, Injection MoldingAppe.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | 2"/min; ASTM D638 |
A. Schulman CP814-01 Linear, Low-Density Polyethylene DescriptionCP 814-01 is a linear low-density polyethylene resin with excellent molding characteristics and good low temperature impact. ApplicationCP814-01 meets the specifications contained in FDA .. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | transverse direction; ASTM D882 |
A. Schulman CP80-01 Linear Low-Density Polyethylene DescriptionCP 880-01 natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties.ApplicationCP 880-01 meets FDA Regulation 21 CFR 177.1250(c) 3.1 and 3.2.In.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | machine direction; ASTM D882 |
A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene DescriptionCP 878-01 Natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties. ApplicationCP 878-01 meets FDA Regulation 21 CFR 177.1520(c)3.1 and 3.2.In.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
Trelleborg Horda Cable E8551 Strippable Semiconductive Shielding E8551 is a vulcanizing, strippable semiconductive compound, designed for both XLPE and EPDM rubber insulated cables and use in both dry and steam curing processes.E8551 meets the requirements as bel.. |
|||
Tensile Strength, Yield | >= 11.0 MPa | >= 1600 psi | |
Trelleborg Offshore Vikotherm™ 73185 Insulative Elastomer Vikotherm™ is a rubber elastomer chemically modified to provide very high insulating characteristics while maintaining its inherent rubber properties in respect of seawater resistance, pressure res.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | machine direction; ASTM D882 |
A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene DescriptionCP 878-01 Natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties. ApplicationCP 878-01 meets FDA Regulation 21 CFR 177.1520(c)3.1 and 3.2.In.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | 2 in/min, Type IV bar; ASTM D638 |
Chevron Phillips Marlex® 7104 LLDPE Sheet Extrusion Resin Type: Hexene CopolymerCharacteristics: Outstanding ESCRGood melt strengthExcellent flexibilityGood processabilityGood glossHigh COFApplications: Landfill coversFlat and round-die productsCoext.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DNDA-1081 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-1081 NT 7 is produced using UNIPOL™ PE process technology. It is intended for high-speed injection molding of thin walled parts such as downguaged lids. Information provided by Dow |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DNDA-7340 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-7340 NT 7 LLDPE resin is well-suited for use in blow molding applications such as small, squeezable bottles, as well as, extruded flexible hoses and tubing. DOW DMDA-7340 NT 7 resin is als.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow 959S Linear Low Density Polyethylene (LDPE) DOW Polyethylene 959S is a medium molecular weight distribution homopolymer. This resin has good process-ability over a wide range of molding conditions. Typical applications include lids. It com.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D-638 |
Axiall 8642 Moldings & Extrusions Flexible PVC General purpose, fungus resistant extrusion and molding compound recommended for weatherstrips and tubings.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ISO R 527 |
Addiplast Addilene J 420 K24 Polypropylene Copolymer High densityInformation provided by Addiplast. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | heat aged one week at 300ºF |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 40 PHR N330 (HAF) Black MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D412 |
Teknor Apex APEX® 3210-70 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Sterilizable, Radiation Uses-Automotive Applications, Connectors, Non-specific Food Applications, Ge.. |
|||
Tensile Strength, Yield | 11.0 MPa | 1600 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Suprex Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 11.0 - 43.0 MPa | 1600 - 6240 psi | Average value: 26.2 MPa Grade Count:322 |
Overview of materials for High Density Polyethylene (HDPE), Injection Molded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Injection Molded". Each property range of values reported is minimum a.. |