Polymer Property : Tensile Strength, Yield = 160000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	1100 MPa	160000 psi
Pacific Sintered Materials FN-262-T(HT) High Strength Nickel Steel Powdered Metal High strength, good impact resistant material for mechanical components. Excellent hardenability.Equivalent MPIF Specification: FN-0408-155HTAll information provided by Pacific Sintered Metals.
Tensile Strength, Yield	1100 MPa @Strain 0.200 %	160000 psi @Strain 0.200 %
FloMet 17-4PH Stainless Steel, Heat Treated (H-900) FloMet provides precision miniature components through metal injection molding (MIM). Metal powders are mixed with thermoplastic binders to form a homogeneous mixture, with approximately 60% volume..
Tensile Strength, Yield	>= 1103 MPa	>= 160000 psi	0.2% proof
Kobe Steel KS15-5-3 Beta Titanium Alloy, AMS 4914, Solution treated and aged, Forgings Nominal Composition: Ti-15 Mo-5 Zr-3 AlApplications: Implant materials for orthopedics, erosion shields, gold club heads. Features:Super high strength.Information provided by Kobe Steel
Tensile Strength, Yield	>= 1103 MPa	>= 160000 psi	0.2% proof
Kobe Steel KS-6-2-4-6 Alpha-Beta Titanium Alloy, AMS 4981, Solution treated and aged. Thickness ≤ 3 in. Nominal Composition: Ti-6 Al-2 Sn-4 Zr-6 Mo Applications: Jet engine parts. Features:High strength, excellent balance between strength and toughness.Information provided by Kobe Steel
Tensile Strength, Yield	1100 - 1320 MPa	160000 - 191000 psi
Materion Beryllium Copper Alloy 25 Rod and Bar; HT (TH04) Temper; up to 9.5 mm (UNS C17200) Treatment required for max strength: 2-3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materi..
Tensile Strength, Yield	1100 - 1320 MPa	160000 - 191000 psi
Materion Beryllium Copper Alloy 25 Strip; 1/2HT (TH02) Temper (UNS C17200) Treatment required for max strength: 2 hrs @ 315ÂºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 73%Superficial Hardness: 30N 58-6..
Tensile Strength, Yield	1100 - 1320 MPa	160000 - 191000 psi
Materion Beryllium Copper Alloy 25 Tube; HT (TH04) Temper; up to 9.5 mm o.d. (UNS C17200) Treatment required for max strength: 2-3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materi..
Tensile Strength, Yield	1100 - 1320 MPa	160000 - 191000 psi
Materion Beryllium Copper Alloy M25 Rod and Bar; HT (TH04) Temper; up to 9.5 mm (UNS C17300) Treatment required for max strength: 2-3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materi..
Tensile Strength, Yield	1100 MPa	160000 psi	Typical
Industeel FORA 400 400 HB Wear Resistant Steel Description: FORA 400 is a water quenched martensitic steel, with a typical hardness of 400HB (42.5 HRC), constituting a real answer to abrasive wear. Thanks to its toughness, its elevated hardness,..
Tensile Strength, Yield	1103 MPa	160000 psi	177Â°C Temper Temperature
Latrobe LescalloyÂ® 16NCD13 VAC-ARC High Strength Alloy Steel 16NCD13 VAC-ARC is a premium quality low alloy, carburizing casehardenable vacuum arc remelted steel which takes its name from the French industry designation. In the carburized condition, its high ..
Tensile Strength, Yield	1100 - 1320 MPa	160000 - 191000 psi
Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; HT (TH04) Temper; up to 9.5 mm Thickness (UNS C17200) Treatment required for max strength: 2 hrs @ 330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Yield	1100 - 1250 MPa	160000 - 181000 psi	Solution Annealed & Aged
Materion Beryllium Nickel M220C Information supplied by Brush Wellman Engineered Materials.Brush M220C is characterized by high levels of strength, hardness, and thermal conductivity combined with excellent resistance to wear, cor..
Tensile Strength, Yield	1100 MPa @Strain 0.200 %	160000 psi @Strain 0.200 %	Precipitation Hardened. Value at room temperature
Special Metals INCOLOYÂ® Alloy 907 A nickel-iron-cobalt alloy with additions of niobium and titanium for precipitation hardening. It has the low coefficient of expansion and high strength of INCOLOY alloy 903 but with improved notch..
Tensile Strength, Yield	1100 MPa @Strain 0.200 %	160000 psi @Strain 0.200 %	Precipitation Hardened. Value at room temperature
Special Metals INCONELÂ® Alloy 718 Developed in the early 1960's, IN718 is still considered the material of choice for the majority of aircraft engine components with service temperatures below 1200Â°F (650Â°C). Inconel 718 is a..
Tensile Strength, Yield	>= 1100 MPa	>= 160000 psi	After bake hardening
SSAB Tunnplat DocolÂ® 1200 DP High-strength Steel The steels are annealed at temperatures between 750Â°C and 850Â°C, depending on the grade of steel, and then are hardened by quenching in water. Tempering is the next stage, in which the steel ..
Tensile Strength, Yield	1100 MPa	160000 psi
ThyssenKrupp SECURE 450 Structural Steel This Material Specification applies to the liquid-quenched and tempered high-strength special steel SECURE 450 with a hardness between 400 - 480 HBW for civil use from 4 up to 20 mm thickness.Applic..
Tensile Strength, Yield	>= 1100 MPa	>= 160000 psi
ThyssenKrupp XABO® 1100 Structural Steel This Material Specification applies to liquid-quenched and tempered heavy plates from 4 up to 40 mm in thickness, made of the high-strength special structural steel XABO® 1100.Application: The stee..
Tensile Strength, Yield	1100 MPa @Strain 0.200 %	160000 psi @Strain 0.200 %	Typical
TIMET TIMETAL® 6-2-4-6 Titanium Alloy (Ti-6Al-2Sn-4Zr-6Mo), Typical This entry has typical property data. Other database entries for TIMETAL® 6-2-4-6 have tensile and fatigue data for specific sample conditions.High-Strength, Intermediate Temperature AlloyFeatures..
Tensile Strength, Yield	1100 MPa	160000 psi
Wingate Alloys Winco-Tuf 36 High Strength Wear Plate Quenched and Tempered for extreme abrasion and impact. Winco-Tuf 36 has excellent toughness at high hardness and in heavy sections. For severe impact and abrasions. Advantages: Maximum resistance to..
Tensile Strength, Yield	1100 MPa @Strain 0.200 %	160000 psi @Strain 0.200 %	Typical
TIMET TIMETAL® 17 Titanium Alloy (Ti-5Al-2Sn-4Mo-2Zr-6Mo); Aged Billet/Bar Features: High strength, deep hardenable forging alloy primarily for jet engines. Allows heat treatment to a variety of strength levels in sections up to 6 inches. Offers good ductility and toughnes..
Tensile Strength, Yield	>= 1100 MPa @Strain 0.200 %	>= 160000 psi @Strain 0.200 %
CLAL-MSX NICLAFOR® 1000 THX Quenched/Precipitation Heat Treated, Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Yield	1100 MPa	160000 psi	when tempered around 950°F
Carpenter Stentor® Alloy Tool Steel (Oil-Hard) (AISI 02) An oil-hardening alloy with excellent size change properties, Stentor tool steel is especially suited for general purpose work in the toolroom. It is safe to harden, and shows little size change or ..
Tensile Strength, Yield	1100 MPa @Temperature 23.0 °C	160000 psi @Temperature 73.4 °F
Assab Steels QRO 90 SUPREME Hot Work Steel QRO 90 SUPREME is a high-performance, chromium-molybdenum-vanadium alloyed hot-work tool steel which is characterized by: Excellent high temperature strength and hot hardnessVery good temper resista..
Tensile Strength, Yield	1100 MPa	160000 psi	after hot stamping
ArcelorMittal Usibor® 1500 Ultra high strength steel, Cold Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to ..
Tensile Strength, Yield	1100 MPa	160000 psi	after hot stamping
ArcelorMittal Usibor® 1500 Ultra high strength steel, Hot Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to ..
Tensile Strength, Yield	1100 MPa @Temperature 204 °C	160000 psi @Temperature 400 °F
ATI Allvac® 718Plus™ Nickel Superalloy Allvac 718Plus alloy (UNS N07818) is a precipitation hardened nickel-base material that exhibits high temperature tensile strength and stress rupture performance. This alloy is designed to have the..
Tensile Strength, Yield	1100 MPa	160000 psi	after hot stamping
ArcelorMittal Usibor® 22MnB5 Ultra high strength steel, Cold Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to ..
Tensile Strength, Yield	1100 MPa	160000 psi	after hot stamping
ArcelorMittal Usibor® 22MnB5 Ultra high strength steel, Hot Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to ..
Tensile Strength, Yield	1103 MPa @Strain 0.200 %, Temperature -18.0 °C	160000 psi @Strain 0.200 %, Temperature -0.400 °F
Carpenter Custom 450® Stainless Steel, Condition H1050 (Age Hardened 566°C) Data provided by Carpenter Technology Corporation.Custom 450® stainless is a martensitic age-hardenable stainless steel which exhibits very good corrosion resistance (similar to that of Stainless T..
Tensile Strength, Yield	1100 MPa @Strain 0.200 %	160000 psi @Strain 0.200 %	Precipitation Hardened
Special Metals INCOLOY® Alloy 903 A nickel-iron-cobalt alloy with additions of niobium, titanium, and aluminum for precipitation hardening. The alloy combines high strength with a low and constant coefficient of thermal expansion a..