Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 19.0 MPa | >= 2760 psi | ISO/R 527 |
Okulen® 2000 PE-UHMW, SGB OKULEN® 2000 is an ultra high molecular low pressure polythylene with a molecular weight of > 7.000.000 g/mol plus additives for the improvement of specific material properties. It has an antistati.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ISO 527 |
Quadrant EPP Cestidur™ Polyethylene Data provided by Quadrant Engineering Plastic Products for polymers in their European product line. |
|||
Tensile Strength, Yield | 19.0 - 28.0 MPa | 2760 - 4060 psi | |
Reliance Industries Polypropylene Impact Copolymer Typical properties of Reliance - Repol Polypropylene grades. Properties depend on rubber content, presence of nucleating agent, MFIInformation provided by Reliance Industries |
|||
Tensile Strength, Yield | 19.0 MPa | 2750 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N774 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50 mm/min; ASTM D638 |
ICO Polymers ICORENEâ„¢ 115-1325 LMDPE Rotational Molding Resin Description: ICORENE 115-1325 is a linear medium density polyethylene developed for use in rotational molding. It is an easy processing material with good surface gloss, scratch resistance and gene.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50 mm/min; ASTM D638 |
ICO Polymers ICORENEâ„¢ 190-1325 LMDPE Rotational Molding Resin Description: ICORENE 190-1325 is a linear medium density polyethylene copolymer developed for rotational molding. It has a good balance of properties such as toughness, easy flow and stiffness. Key.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50 mm/min; ISO 527-1,-2 |
Inno-Comp INNOPOL® CS 2-9524 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer INNOPOL® CS 2-9524 is a 20% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-9524 is dev.. |
|||
Tensile Strength, Yield | 19.0 MPa @Strain 0.200 %, Temperature 1149 °C |
2760 psi @Strain 0.200 %, Temperature 2100 °F |
|
Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ISO R527-1 |
LyondellBasell Hifaxâ„¢ CA187 Thermoplastic Olefin Resin Key Features: medium melt flow, medium modulus, paintable thermoplastic elastomeric olefin resin, excellent paintability, excellent surface appearance, good impact and stiffness balanceApplications:.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ISO 527-1, -2 |
LyondellBasell Hostacomâ„¢ BG749GC/1 Polypropylene Copolymer Description: Hostacomâ„¢ BG749GC/1 medium melt flow, 1,100 MPa flexural modulus, UV-stabilized, precolored, 20% calcium carbonate-filled polypropylene copolymer resin has an excellent combination.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR (Asia Pacific) LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MB008S PP LNP* THERMOCOMP* MB008S is a compound based on Polypropylene resin containing 40% Glass Bead. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP MB008S PP LNP* THERMOCOMP* MB008S is a compound based on Polypropylene resin containing 40% Glass Bead. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
SCG Chemicals EL-Leneâ„¢ M70 Butene (C4) Rotational Molding Resin Color compound resin available in pellet / powder formKey Characteristics:High flowFast cycle timesExcellent surface finishingTypical Applications: Complex/Intricate products, high volume/short cyc.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2750 psi | ASTM D638 |
Washington Penn Medium Impact Copolymer 20% Calcium Carbonate Filled Calcium carbonate-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug pa.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
A. Schulman POLYFLAM™ CB 3229 Medium Flow, High Impact Copolymer Polypropylene DescriptionPolyfort® CB 3229 is a medium flow, high impact copolymer polypropylene product for injection molding applications.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
UBE PAE1201U Nylon Elastomer Description: UBESTA Nylon 12 ElastomerInformation provided by UBE. |
|||
Tensile Strength, Yield | 19.0 MPa | 2750 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N774 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ISO 527-2 |
ExxonMobil Exxtral™ BMV 201 Performance Polyolefin Product Description: A specialty thermoplastic olefin injection molding compound resin with good flow, cold temperature impact resistance, low CLTE, and excellent paintability for large automotive e.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
Dow DS6D82 Polypropylene Random Copolymer Resin OverviewConsistent processabilityGood optical propertiesLow temperature heat sealComplies with U.S. FDA 21 CFR 177.1520 (c)3.1aDOW DS6D82 Polypropylene Resin is intended for use as a heat seal coati.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2750 psi | molded and tested in accordance with ASTM D 4101; ASTM D638 |
Dow DS6D82 Polypropylene Resin DOW DS6D82 is intended for use as a heat seal coating on oriented polypropylene (OPP) film.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braskem in July 2011. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
Braskem CP 195 Injection Molding Polypropylene Description: CP 195 is a very high melt flow rate heterophasic copolymer developed for high speed injection moulding machines and high productivity thin-walled injection moulded parts. The product f.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436C30L Calcium Reinforced |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | ISO 527 |
Total Lacqtene® 2002 TN 40 HDPE, blow molding, pipe, sheet
(discontinued **) LACQTENE® 2002 TN 40 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer.Information provided provided by Total Petrochemicals.Total Petrochemic.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | after aging 1 week @ 135°C; ASTM D638 |
Trelleborg Horda Cable E7310 Bonded Insulation Shielding And Conductor Screen E7310 is a silane crosslinkable semiconductive compound for medium voltage cables. The material is designed as a conductor screen and bonded insulation shielding.E7310 meets the requirements as bel.. |
|||
Tensile Strength, Yield | 19.0 - 51.0 MPa | 2760 - 7400 psi | Average value: 31.7 MPa Grade Count:29 |
Overview of materials for Cellulose Acetate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate, Molded". Each property range of values reported is minimum and maximum values of appr.. |
|||
Tensile Strength, Yield | 19.0 MPa @Strain 300 %, Thickness 0.760 mm |
2760 psi @Strain 300 %, Thickness 0.0299 in |
extruded sheet; ASTM D412 |
BASF Elastollan® 1185A10Y Wire & Cable Grade Polyurethane Elastomer Compliant with NSF Standard 61 (Drinking water contact). As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation. |
|||
Tensile Strength, Yield | 19.0 MPa | 2760 psi | 2.0 in/min; ASTM D638 |
Ineos Nova Zyntar® 779 High Performance Flame Retardant Polystyrene
(discontinued **) Non-Decabromodiphenyl Oxide, Color stable, Custom colorsApplications: Injection molding, Alternative to flame retardant ABS, Copiers, Computer monitors, Office equipmentThis is an impact grade of po.. |
|||
Tensile Strength, Yield | 19.0 MPa | 2750 psi | ASTM D-638 |
Axiall 15900 Wire & Cable Flexible PVC Non-lead stabilized insulation compound recommended for TW and 80C Class 43 applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 19.0 - 42.1 MPa | 2760 - 6110 psi | Average value: 32.8 MPa Grade Count:128 |
Overview of materials for Polypropylene, Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Extrusion Grade". Each property range of values reported is minimum and maximum values of.. |