Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2 in per min; ASTM D638 |
Network Polymers NPP 25-1002 Description: Copolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Petromont 3100 High Density Polyethylene Resin Petromont HDPE 3100 is a high density polyethylene resin produced using the UNIPOL® Process. This resin is intended for injection moulding of high performance products such as pails, industrial par.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | (2 in/min); ASTM D638 |
Phillips 66 COPYLENE® CR350CL-01 Polypropylene, Random Copolymer, Clarified COPYLENE™ CR350CL-01 is a clarified, easy molding high melt flow polypropylene random copolymer resin with good see-through and contact clarity in injection molding applications.Applications: House.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Eastman Tenite Butyrate 465E2R30012 Natural, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 12%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4110 psi | Crosshead Speed 2 in/min; ASTM D638 |
LyondellBasell Alathon® M5363 High Density Polyethylene ApplicationsALATHON L 4912 is a high molecular weight, high density copolymer with a broad molecular weight distribution. This resin provides excellent stiffness and a good balance of film properti.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2"/min; ASTM D638 |
LyondellBasell Lupolen® 5261 Z Q 456 High Density Polyethylene, Pipe and Sheet Extrusion Grade Lupolen 5261 Z Q 456 is a high density polyethylene (HDPE) with high melt viscosity for ram extrusion of peroxide crosslinked pipes (PE-Xa). The product is supplied as a nominal 20 mesh (840 µm) .. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
I. Stern 2335C Prime Clarified Random Copolymer Polypropylene Features:High flow characteristicsFDASee-through and contact clarityFood contact acceptableApplicationsContainersBottlesStorage boxesToysInformation provided by I. Stern & Co. Inc. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2 in/min; ASTM D638 |
Ineos B4020N1332 Polyethylene Copolymer This is a unique high density polyethylene copolymer intended for the injection or compression molding of closures for beverages. Because of its high purity and excellent organoleptic properties, t.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Ineos L12Z-00 Polypropylene Impact Copolymer Grade L12Z-00 is a medium melt flow rate, high stiffness and high impact polypropylene copolymer. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Techmer ES Statiblend® HDPE C BK Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified FillerReinforFeatures: ConductiveUL File Number: E157318Appearance: BlackTPCI# 9411115Information provided by TP Composites.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene DescriptionPolypropylene PP 1116-01 is a molding grade copolymer polypropylene with improved low temperature toughness and good room temperature toughness. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene DescriptionPolypropylene PP 828S-01 is a medium impact molding grade created for applications needing good impact and higher H.D.T., such as tote bins, automotive ducting and housings. Information p.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Washington Penn Homopolymer Polypropylene 20% Calcium Carbonate Filled Calcium carbonate-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug pa.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene DescriptionPolypropylene PP 1116-01 is a molding grade copolymer polypropylene with improved low temperature toughness and good room temperature toughness. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene DescriptionPolypropylene PP 1116-01 is a molding grade copolymer polypropylene with improved low temperature toughness and good room temperature toughness. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Eastman Tenite Butyrate 530A3720016 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 12%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
ExxonMobil HDPE BA53-055 High Density Polyethylene Resin Product Description: BA53-055 is a high molecular weight, high density polyethylene copolymer.Availability: Latin America, North America and South America Additive: Antistatic: NoApplications: Dru.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
ExxonMobil HDPE HD 7800P High Density Polyethylene Copolymer Resin Product Description: HD 7800P is a pipe extrusion grade high density polyethylene copolymer offering an excellent combination of stiffness and stress crack resistance. This material meets or exceeds.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
ExxonMobil HDPE HYA021L High Density Polyethylene Resin Product Description: HYA021L is a molecular weight, high-density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity.Availability: Latin A.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
ExxonMobil Paxon™ AA53-003 Pipe Extrusion Resin Product Description: AA53-003 is a pipe extrusion grade high density polyethylene copolymer offering an excellent combination of stiffness and stress crack resistance. This material meets or exceeds.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4110 psi | ASTM D638 |
Entec Hypel® PEHD8/.953 HDPE Available in North America Features: Food Contact Acceptable and High DensityAgency Ratings: FDA 21 CFR 177.1520RoHS Compliant Form: Pellets Information provided by Entec |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DMDA-8920 NT 7 High Density Polyethylene Resin DOW DMDA-8920 NT 7 is produced using UNIPOL™ process technology. It is intended for use in a broad range of injection molding applications such as housewares, toys, food containers and pails. Info.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Dow INSPIRE™ D560.00 Developmental Performance Polymer D 560.00 Performance Polymer has consistent processability, high gloss, good regrind stability, and contains U.V. stabilizers for increased weatherability. D 560.00 Performance Polymer is intended f.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2" per min, Type IV; ASTM D638 |
Amco PRIMATOP HDPE 004955HP Blow Molding Polyethylene HDPE 003955PZ features zinc stearate additive and is used for injection blow molding.Former A-Top Polymers product; part of Amco product line since 2013. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
ExxonMobil Paxon™ BA7794 Sheet Extrusion and Blow Molding Resin
(discontinued **) BA7794 is a 25% talc-filled, high molecular weight, high density polyethylene. This color match-able material has been specifically developed as a cost effective resin for applications which requir.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Lubrizol Stat-Rite® SIS535 Static Control System Product Description: Stat-Rite® SIS535 is a static dissipative HIPS alloy. Stat-Rite SIS535 utilizes the patented Stat-Rite inherently dissipative polymer (IDP) alloy system to provide clean, perma.. |