Polymer Property : Tensile Strength, Yield = 33400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	230 MPa	33400 psi	ISO 527, ASTM D638
Nilit Nilamid B3 H G10 50% Glass Fiber Reinforced PA6 Description: Nilamid B3 H G10 is a product that combines outstanding strength and stiffness with good moldability and good impact strength. It is widely used for structural applications.Key characte..
Tensile Strength, Yield	230 MPa	33400 psi	ISO 527-2
Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA) (Unverified Data**) Ixef 1524 is a 50% glass-fiber reinforced, halogen-free flame retardant polyarylamide which exhibits high strength and stiffness, good surface gloss, and excellent creep resistance. - Black: Ixef 15..
Tensile Strength, Yield	230 MPa	33400 psi	ASTM D638
LNP Thermocomp® EC-1006 EM Polyetherimide, Carbon Fiber Reinforcement (discontinued **) Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are st..
Tensile Strength, Yield	230 MPa @Thickness 3.20 mm	33400 psi @Thickness 0.126 in	5mm/min; ASTM D638
LG Chemical LUMID GP2500B(W) PA66+GF50%, General Purpose Feature: Injection Molding, PA66+GF50%, General PurposeApplication: Automotive (Gear Shift Housing)CAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical
Tensile Strength, Yield	230 MPa @Strain 0.200 %, Temperature 980 Â°C	33400 psi @Strain 0.200 %, Temperature 1800 Â°F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370Â°C (700Â°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	230 MPa @Temperature 870 Â°C	33400 psi @Temperature 1600 Â°F
Haynes HastelloyÂ® alloy X 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Yield	230 MPa	33400 psi	ISO 527 type 1 A
Solvay TECHNYLÂ® A 218 V43 Black 21 N PA66, 43% glass fiber, DRY Description: Polyamide PA66, reinforced with 43% of glass fiber, heat stabilized, for injection molding.Available in: North AmericaProduct Applications: TECHNYLÂ® A 218 V43 is used in all sectors ..
Tensile Strength, Yield	230 MPa	33400 psi	ASTM D638
Solvay TECHNYLSTARâ„¢ AFX 218S V50 PA6, 50% glass filled, DRY Description: High stiffness materials TECHNYLSTAR Polyamide 66, reinforced with 50% of glass fiber, heat stabilized for injection molding. Characterized by a high fluidity of the melt. Available in:..
Tensile Strength, Yield	230 MPa	33400 psi	ISO 527-2
Solvay Specialty Polymers KalixÂ® 2855 Polyamide, High Performance (HPPA), Glass Fiber KalixÂ® 2855 is a 27% bio-sourced, PA 6,10-based compound with 55% by weight glass fiber reinforcement. This material is formulated to provide maximum strength, stiffness, impact resistance, and p..
Tensile Strength, Yield	230 MPa	33400 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF008 PA 66 LNP* THERMOCOMP* RF-1008 is a compound based on Nylon 66 resin containing Glass Fiber.
Tensile Strength, Yield	230 MPa	33400 psi	ISO 527-2
Solvay Specialty Polymers IxefÂ® 1524 Polyarylamide (PARA), 50% Glass Fiber (Dry) IxefÂ® 1524 is a 50% glass-fiber reinforced, halogen-free flame retardant polyarylamide which exhibits high strength and stiffness, good surface gloss, and excellent creep resistance.Features: Bro..
Tensile Strength, Yield	230 MPa	33400 psi	ASTM D638
Techmer ES HiFillÂ® TPX-HTN-01092 A 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Heat StabilizerFeatures: Heat Stabilized and High Temperature StrengthInformat..
Tensile Strength, Yield	230 MPa	33400 psi	ASTM-D638
Polyram PlusTek PA301G50 Nylon 6.6, Heat Stabilized, 50% Glass Fiber Heat stabilized, 50% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Strength, Yield	230 MPa	33400 psi	ASTM D638
E-Polymers TEKAMID® TA250G45 , 45% Glass Fiber Reinforced PA66, DAM 45% Glass Fiber Reinforced, Good surfaceInformation provided by E-Polymers Co. Ltd.
Tensile Strength, Yield	>= 230 MPa	>= 33400 psi
AK Steel ASTM A 1018, Grade 33 Hot Rolled Carbon Steel, Structural Steel (SS) Information provided by AK Steel
Tensile Strength, Yield	>= 230 MPa	>= 33400 psi
AK Steel ASTM A 570, Grade 33 Hot Rolled Carbon Steel, Structural Quality (SQ) For gauges up to 0.229", ASTM A 570 must be specified, gauges >0.230", ASTM A 907 must be used. Items 0.180 to 0.230" gauge which are >48" wide may be ordered to either A 570 or A 907.Information p..
Tensile Strength, Yield	>= 230 MPa	>= 33400 psi
AK Steel Type 1 & 2, Grade 33 Cold Rolled Carbon Steel, Structural Steel (SS) Information provided by AK Steel
Tensile Strength, Yield	230 MPa	33400 psi
Ametek Ultra 303L P/M Stainless Steel, Sintered from 6.35 g/cc Green Density Ametek's patented Ultra Stainless Steels™ are produced by alloying the conventional austenitic compositions with a small amount of a copper-nickel-tin alloy. This results in a marked improvement i..
Tensile Strength, Yield	230 MPa	33400 psi
Ametek Ultra 316L P/M Stainless Steel, Sintered from 6.49 g/cc Green Density Ametek's patented Ultra Stainless Steels™ are produced by alloying the conventional austenitic compositions with a small amount of a copper-nickel-tin alloy. This results in a marked improvement i..
Tensile Strength, Yield	230 MPa	33400 psi	v = 50 mm/min; ISO 527-2
CENTROPLAST CENTROMID 6.6 CF 20 Polyamide 6.6 carbon fiber This material has very high strength and a high operating temperature. It can be used for precision components, drive parts and housings.Information provided by CENTROPLAST Engineering Plastics GMB..
Tensile Strength, Yield	>= 230 MPa	>= 33400 psi
AK Steel ZINCGRIP® 230, Grade 33 Hot Dip Galvanized Carbon Steel, Structural Steel (SS) Information provided by AK Steel
Tensile Strength, Yield	230 MPa	33400 psi
Ametek Ultra 304L P/M Stainless Steel, Sintered from 6.38 g/cc Green Density Ametek's patented Ultra Stainless Steels™ are produced by alloying the conventional austenitic compositions with a small amount of a copper-nickel-tin alloy. This results in a marked improvement i..
Tensile Strength, Yield	230 MPa @Thickness 5.00 - 12.0 mm	33400 psi @Thickness 0.197 - 0.472 in	Typical L-T Direction; 0.2% Offset
Aleris HOGAL 5558 Aluminum 5026 H14/H34 HOGAL 5558 is produced according to EN AW-5026.Information provided by Aleris.
Tensile Strength, Yield	230 MPa	33400 psi	ASTM-D638
Polyram Polytron A40N02 Nylon 66, 40% Long Fiber 40% LONG FIBER GLASS REINFORCED NATURAL NYLON 6.6 HEAT STABILIZED, UV STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind.
Tensile Strength, Yield	230 MPa @Strain 0.200 %, Temperature 538 °C	33400 psi @Strain 0.200 %, Temperature 1000 °F
Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Tensile Strength, Yield	230 MPa	33400 psi	ASTM-D638
Polyram Polytron A40B02 Nylon 66, 40% Long Fiber A 40% LONG FIBER GLASS REINFORCED BLACK NYLON 6.6 HEAT STABILIZED, UV STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind.