Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
Plaskolite PETG Mirror Sheet Versatile fabrication properties with good impact strength, good design flexibility, and speed of fabrication.Data provided by the manufacturer, Plaskolite, Inc. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | |
Ineos ABS Lustran® QE 1088 FC, Injection Grade
(discontinued **) Injection molding grade, high impact, medium gloss.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholdi.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PX6120 PPE+PS (Asia Pacific) Noryl PX6120 is an unfilled material with good flow, high Impact and chemical resistance against cleaners. Noryl PX6120 is developed for personal care appplications. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DP003 PC LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DP003 PC (Asia Pacific) LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DX96651 PC (Asia Pacific) LNP LUBRICOMP* DX96651 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ISO 527 type 1 A |
Solvay TECHNYL® A 303 Natural FA PA66, Conditioned Description: Unreinforced polyamide PA66, very high viscosity, for extrusion.Available in: Europe Product Applications: TECHNYL® A 303 Natural FA offers three main advantages: high impact resista.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP QP004 PA 6/10 LNP* LUBRICOMP* QP004 is a compound based on Nylon 6/10 containing 20% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Valox® 357 PBT PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 357 PBT (Asia Pacific) PBT + PC, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ357 PBT+PC Valox* Resin IQ357: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® IQ357U PBT+PC (Asia Pacific) Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50mm/min; ISO 527 |
Styrolution Luran® S 777 K ASA Luran S 777 K is an easy flowing injection molding ASA grade with good toughness and heat distorsion resistance. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ISO 527 |
Styrolution Novodur® 450 ABS Novodur 450 is an injection molding grade of ABS with medium impact and high gloss.Information provided by Styrolution |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | |
Styrolution NOVODUR® P3H-AT ABS, Injection Grade Injection molding grade, antistatic, high gloss, improved chemical and dynamic resistance.Applications: Housings for telephones and household appliances. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp MCR13S PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MCR13S is a compound based on Polypropylene resin containing Carbon Fiber, Barium Sulfate. Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min; ASTM D638 |
Styron MAGNUMâ„¢ 8391 Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ 8391 ABS combines an excellent glossy appearance with high flow and medium impact performance. The mass continuous process) ABS technology of Styron ensures an ABS resin that .. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | SABIC - Japan Method |
SABIC Innovative Plastics Valox® V3900WX PBT+PC PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL BN9003G PPE+HIPS PPE+PS blend. Unfilled. Blow molding. Excellent balance of impact and surface aesthetics. Suitable for automotive exterior components including spoilers. |
|||
Tensile Strength, Yield | 48.0 MPa @Temperature 100 °C |
6960 psi @Temperature 212 °F |
ISO 527-2 |
Borealis Xmod™ GB305HP High Performance 35% Glass Fiber Reinforced Xmod GB305HP is reinforced with 35% chemically coupled glass fibers and based on a specific Polymer matrix material that is bringing excellent mechanical properties (biaxial impact behavior) as well.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ISO 527 |
Eastman Drystar 0325 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
Eastman Spectar® Clear Copolyester for Thermoforming Applications:Decorative Light-Transmitting PanelsHeavy gauge sheet displaysKey Attributes:Easy to print and decorateExcellent clarityExcellent thermoforming characteristicsGood chemical resistanceOd.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D 638 |
Cossa Polimeri ESTADIENE 1030 T V0 Flame Retardant ABS Acrylonitrile Butadiene StyreneFlame retardant class V0, PBDE free, high thermal resistance, good impact resistance, high gloss, good light resistance, good processabilityInformation provided by Cos.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min |
Arkema Group Rilsan® AECN TL Nylon 12, Cable Sheathing Grade (Dry) Designation ISO 1874-PA12,KHL,14-010Extrusion grade for the sheathing of wires and cables. Available colors: natural and orange. Heat and light stabilized.Low melt viscosity. High speed extrusion. V.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | 2 in/min; ASTM Test |
BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min |
Arkema Group Rilsan® MB 3000 Nylon 11, Sheathing Grade (Conditioned) Designation ISO 1874-PA11,MF,12-010Polyvalent rigid grade for injection molding and sheathing of cables. Available color: natural. Flame retardant agent, halogen free. Fire-resistant. Easy to be pro.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
E-Polymers Tekaloy® T80 , Dimensional Stability PBT/ABS Alloy Dimensional StabilityInformation provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ISO 527B |
Ineos Nova 201 Crystal Polystyrene High Heat Extrusion Grade
(discontinued **) Excellent heat resistance, Superior melt strengthApplications: Foam insulation, Oriented polystyrene sheet (OPS), XPS food packaging, Sheet and profile extrusionProperties were determined on injecti.. |
|||
Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
Ineos Nova 1301 High Heat Crystal Polystyrene High heat resistance, High strength, Good processing characteristics, USP Class VIApplications: Electronics packaging, Medical packaging, Cosmetic cases, Profile extrusionExposure to gamma radiation.. |
|||
Tensile Strength, Yield | 48.0 - 48.0 MPa @Temperature 100 - 100 °C |
6960 - 6960 psi @Temperature 212 - 212 °F |
Average value: 48.0 MPa Grade Count:1 |
Overview of materials for Polypropylene with 40% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Glass Fiber Filler". Specific grades with glass content between 35% and 44% are i.. |