- Polymer Property : Tensile Strength, Yield = 4900 psi
Polymer Property : Tensile Strength, Yield = 4900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | Type I, 51 mm/min; ASTM D638 |
| PolyOne Maxxam™ PD 2201 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | 2 in per min, tangent; ASTM D638 |
| Network Polymers NPP 30-2000 TF40 Description: 40% Talc Filled Homopolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 8% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Fiberfil® PP-60/TC/13 BL8860 Polypropylene Homopolymer, 13% Talc Filled Information provided by FIBERFIL Engineered Plastics |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| JPJ Technologies PP H35S Homopolymer for Injection Molding PP H35S is specifically developed for producing injection molding articles for general purpose applications. It gives consistent processability and high gloss in the products. Application: General u.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Techmer ES Plastiblend® ABS 8004 UV MB Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV Resistance and High Heat ResistanceTPCI# 6816121Information provided by TP Composites, Inc. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Techmer ES Plastiblend® ABS 8014 Availability: North AmericaForms: PelletsProcessing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Techmer ES Plastiblend® ABS 8004 Availability: North AmericaForms: PelletsFeatures: General Purpose and High Impact ResistanceInformation provided by TP Composites, Inc. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3487-01 is a special homopolymer polypropylene formulated with a long term heat aging resistance. This material has excellent resistance to chemicals and solvents. High.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3487-01 is a special homopolymer polypropylene formulated with a long term heat aging resistance. This material has excellent resistance to chemicals and solvents. High.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | 2" (50mm) per min.; ASTM D638 |
| Formosa Plastics Formolene® 4101M Staple Fiber and Injection Molding Polypropylene HomopolymerApplications: Staple Fiber and General Purpose Injection MoldingFormolene 4101M is a medium viscosity, highly isotactic polypropylene homopolymer designed for Staple Fiber and general pur.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3487-01 is a special homopolymer polypropylene formulated with a long term heat aging resistance. This material has excellent resistance to chemicals and solvents. High.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3487-01 is a special homopolymer polypropylene formulated with a long term heat aging resistance. This material has excellent resistance to chemicals and solvents. High.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 310ºF Cure Temperature MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber, No Milling Time MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | 2" (50mm) per min.; ASTM D638 |
| Formosa Plastics Formolene® 4100T Injection Molding Polypropylene Homopolymer with ESCR AdditivesApplications: Closures, small appliances, housewares and toys.Formolene 4100T is a low viscosity, highly isotactic polypropylene homopolymer designed for various injec.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Dow H7012-35RN Polypropylene Homopolymer Resin OverviewGood processabilityGood mold fillingFaster cycle timesContains nucleating additiveComplies with U.S. FDA 21 CFR 177.1520 (c)1.1aDOW H7012-35RN Polypropylene Resin is intended for use in inje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Dow INSPIRE™ 117.00 Performance Polymer 117.00 Performance Polymer is a propylene-based resin intended for use in extrusion blow molding and thermoforming applications where stiffness, toughness, high temperature resistance, and clarity a.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Asahi Kasei Thermofil P-20TC-1161 20% Talc Filled, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N339 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N339 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 8% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Braskem INSPIRE™ 117 Performance Polypropylene Polymer D 117.00 Developmental Performance Polymer is a propylene-based resin intended for use in extrusion blow molding and thermoforming applications where stiffness, toughness, high temperature resistanc.. |
|||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Spartech PP5340 Mica Reinforced Homopolymer Information provided by Spartech |
|||