Polymer Property : Tensile Strength, Yield = 595 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Yield	595 MPa @Strain 0.200 %	86300 psi @Strain 0.200 %
Haynes 214Â® alloy, 0% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	595 MPa @Strain 0.200 %	86300 psi @Strain 0.200 %
Haynes 214Â® alloy, 40% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	595 MPa @Strain 0.200 %, Temperature 425 Â°C	86300 psi @Strain 0.200 %, Temperature 797 Â°F
Haynes 242Â® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Tensile Strength, Yield	595 MPa @Strain 0.200 %, Temperature 760 Â°C	86300 psi @Strain 0.200 %, Temperature 1400 Â°F
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	595 MPa @Strain 0.200 %	86300 psi @Strain 0.200 %
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..