Polymer Property : Tensile Strength, Yield = 70.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
Type 1B, 50mm/min; ISO 527-1/2:1993
Nylacast Cast Nylon 6, Glass Filled
Information provided by Nylacast Ltd.
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
Type 1B, 50mm/min; ISO 527-1/2:1993
Nylacast Impact Nylon 6, Impact Grade
Nylacast Impact has been designed for applications that have a high impact resistance and noise reduction capabilities. It works more effectively in applications where there are high stress. It also..
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
ISO.527 DN.53455
Polimersan Plastics POLIPA® (PA 6) Polyamide
POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc..
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
Injection; ISO 527
Raschig Group 2567 AMC
Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and ..
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
Injection; ISO 527
Raschig Group 2568 AMC
Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s..
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
Injection; ISO 527
Raschig Group 2572 AMC
Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin..
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
Injection and Compression; ISO 527
Raschig Group 3505 Epoxy
Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed..
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
Injection and Compression; ISO 527
Raschig Group 3535 Epoxy
Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack..
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
Injection and Compression; ISO 527
Raschig Group 3536 Epoxy
Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed..
Tensile Strength, Yield 40.0 - 70.0 MPa
5800 - 10200 psi
Injection; ISO 527
Raschig Group RALUPOL® 4385 UP
Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy..
Tensile Strength, Yield 40.0 - 70.0 MPa
5800 - 10200 psi
Injection; ISO 527
Raschig Group RALUPOL® 4806 UP
Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80..
Tensile Strength, Yield 60.0 - 70.0 MPa
8700 - 10200 psi
ISO.527 DN.53455
Polimersan Plastics POLIPA® (PA 6) Polyamide
POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc..
Tensile Strength, Yield 30.0 - 70.0 MPa
4350 - 10200 psi
Average value: 47.9 MPa Grade Count:34
Overview of materials for Acetal Homopolymer, Unreinforced, Impact Grade
This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced, Impact Grade". Each property range of values reported is minimum and m..
Tensile Strength, Yield 40.0 - 70.0 MPa
5800 - 10200 psi
Injection; ISO 527
Raschig Group RALUPOL® 8601 UP
Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic moulding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical stren..
Tensile Strength, Yield 40.0 - 70.0 MPa
5800 - 10200 psi
Injection; ISO 527
Raschig Group RALUPOL® 8602 UP
Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng..
Tensile Strength, Yield 40.0 - 70.0 MPa
5800 - 10200 psi
Injection; ISO 527
Raschig Group SURAPLAST 54 UPA
Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Tensile Strength, Yield 50.0 - 70.0 MPa
7250 - 10200 psi
Injection; ISO 527
Raschig Group SURAPLAST UPA 63 UP
Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Tensile Strength, Yield 58.6 - 70.0 MPa
8500 - 10200 psi
Average value: 63.7 MPa Grade Count:34
Overview of materials for Polycarbonate, Extruded
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Extruded". Each property range of values reported is minimum and maximum values of approp..
Tensile Strength, Yield 34.0 - 70.0 MPa
4930 - 10200 psi
Average value: 53.9 MPa Grade Count:117
Overview of materials for Polycarbonate/PET Polyester Blend
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/PET Polyester Blend". Each property range of values reported is minimum and maximum values..
Tensile Strength, Yield 41.4 - 70.0 MPa
6000 - 10200 psi
Average value: 52.8 MPa Grade Count:13
Overview of materials for Acetal Homopolymer, PTFE-Filled
This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, PTFE-Filled". Each property range of values reported is minimum and maximum values o..
Tensile Strength, Yield 50.0 - 70.0 MPa
7250 - 10200 psi
Injection; ISO 527
Raschig Group MELOPLAS® 180 MF
Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing ..
Tensile Strength, Yield 1.80 - 70.0 MPa
261 - 10200 psi
Average value: 14.2 MPa Grade Count:104
Overview of materials for Thermoplastic Polyurethane (TPUR), Polyether Grade
This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Polyether Grade". Each property range of values reported is minimum a..
Tensile Strength, Yield 13.0 - 70.0 MPa
1890 - 10200 psi
Average value: 24.7 MPa Grade Count:45
Overview of materials for Polypropylene with 30% Calcium Carbonate (CaCO3) Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Calcium Carbonate (CaCO3) Filler". Each property range of values reported is mini..