Polymer Property : Tensile Strength, Yield = 725 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	>= 725 MPa	>= 105000 psi
MetalTek GTD 222Â® Centri-Vac Nickel Cobalt Based Alloy Information provided by MetalTek
Tensile Strength, Yield	725 MPa @Strain 0.200 %	105000 psi @Strain 0.200 %
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	725 MPa @Strain 0.200 %	105000 psi @Strain 0.200 %	Precipitation Hardened. Value at room temperature
Special Metals NIMONICÂ® Alloy 90 A precipitation-hardenable nickel-chromium-cobalt alloy having high stress-rupture strength and creep resistance at temperatures to about 1700Â°F (920Â°C). The alloy also has good resistance to..
Tensile Strength, Yield	>= 725 MPa @Strain 0.200 %	>= 105000 psi @Strain 0.200 %
Schmolz + Bickenbach UGICHROM 4542 Martensitic Chrome Plated Bar Description: Ugichrom combines the high efficiency of micro-fissuring chromium plating with the technology of Ugitechâ€™s most advanced gradesAdvantages: Zero defects guarantee; Low friction coef..
Tensile Strength, Yield	725 MPa @Strain 0.200 %	105000 psi @Strain 0.200 %
ATI Allegheny Ludlum AL 418™ Special (Greek Ascoloy) Martensitic Stainless Steel Uses include engine braces, turbine exhaust components, exhaust struts, stiffeners, and ducts.Information provided by Allegheny Ludlum
Tensile Strength, Yield	<= 725 MPa @Strain 0.200 %	<= 105000 psi @Strain 0.200 %
ATI Allegheny Ludlum Altemp® 718 Nickel-Base Superalloy, Solution Treated Plate, UNS N07718 Allegheny Ludlum Altemp 718 alloy is an austenitic nickel-base superalloy which is used in applications requiring high strength to approximately 760 degrees Celsius and oxidation resistance to appro..
Tensile Strength, Yield	725 MPa @Strain 0.200 %, Temperature 95.0 °C	105000 psi @Strain 0.200 %, Temperature 203 °F
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal..
Tensile Strength, Yield	725 MPa @Strain 0.200 %	105000 psi @Strain 0.200 %
Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we..