Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 86.0 MPa | 12500 psi | dry; ISO 527-1 |
Murtfeldt Murylon® 6 Cast Nylon 6 Murylon® 6 CAST has extremely low levels of residual stress thanks to the casting procedure used to produce it. This material is therefore ideally suited to extensively processed components.Specia.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ASTM D638 |
NYCOA 400 PA 6 nucleated general molding gradeInformation provided by NYCOA, Inc. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ASTM D638 |
NYCOA 512 PA 6 UL and NSF rated nucleated general purpose molding gradeInformation provided by NYCOA, Inc. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50 mm/min; ASTM D638 |
Ovation Polymers OPTRENE 30GF Polypropylene, 30% Glass Reinforced Properties of chemically coupled glass reinforced (30%) polypropylene with high strength and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All .. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | SABIC - Japan Method |
SABIC Innovative Plastics Lexan® LGN2000 PC (Asia Pacific) |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® 12-033
(discontinued **) PRE-ELEC 12-033 is a conductive thermoplastic compound based on a polyacetal copolymer with 30% carbon fiber. PRE-ELEC 12-033 exhibits excellent mechanical properties and electrical conductivity. Te.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO value at 50 mm/min. |
BASF Capron® 5202 HS BK-102 Nylon 66 (Dry)
(discontinued **) Capron 5202 HS BK-102 is an unfilled, heat stabilized, pigmented black nylon 6,6, injection molding compound. It combines strength and stiffness as well as excellent chemical resistance. The additi.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO value at 50 mm/min. |
BASF Capron® 5202 HS Blend Nylon 66 (Dry)
(discontinued **) Capron 5202 HS Blend is a blended, unfilled, heat stabilized, nylon 6,6, injection molding compound. It is also available in natural and pigmented versions. It combines strength and stiffness as wel.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO value at 50 mm/min. |
BASF Capron® 8203C Nylon 6 (Dry)
(discontinued **) Capron 8203C is a high viscosity, nylon 6 extrusion compound, possessing a modified crystalline structure for increased property performance and faster set up for tubing and cable applications. It.. |
|||
Tensile Strength, Yield | 86.0 MPa @Temperature 22.0 °C |
12500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0390 Unsaturated Polyester UP SMC 0390 is a standard low profile SMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surfac.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP EL002 PEI LNP* Lubricomp* EL002 is a compound based on Polyetherimide resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP EX00548C PEI LNP LUBRICOMP* EX00548C is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Clean Compounding System, Wear Resistant. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO 527 type 1 A |
Solvay TECHNYL® A 50H1 PA66, DRY Description: Flame retardant polyamide 66, unreinforced, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This phospho.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® VIC4311 PBT VALOX VIC4311 is a 30% glass filled, impact modified PBT with excellent epoxy adhesion. Automotive underhood applications such as ignition coil housings. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East) DATA ON BK1005 ONLY. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+PS DATA ON BK1005 ONLY. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | SABIC - Japan Method |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000 PC (Asia Pacific) |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl PKN4717 PPE+HIPS (Europe-Africa-Middle East) NORYL PKN4717 is a PPO+PS concentrate for dilution with polystyrene resin for foam extrusion. It is suitable for (microwavable) food packaging and is compliant with US and European food contact regu.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PKN4752 PPE+PS PPE+PS blend. High Heat. Translucent with yellow tint in natural color. FDA compliant. Extrusion and Injection Molding. Typical applications include High Performance Food Packaging, Electronics and .. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PKN4752 PPE+PS (Asia Pacific) PPE+PS. Translucent. FDA compliant. High heat. Extrusion. Microwavable. Food, electrical/electronic packaging uses. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PKN4752 PPE+PS (Europe-Africa-Middle East) NORYL PKN4752 is a translucent, high heat PPO+PS extrusion grade for dilution with polystyrene resin. It is suitable for (microwavable) food packaging and is compliant with US and European food cont.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10 LNP* LUBRICOMP* QFL32 is a compound based on Nylon 6/10 containing 10% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON AE002 ABS LNP* STAT-KON* AE002 is a compound based on ABS resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DFD03 PC LNP* STAT-KON* DFD03 is a compound based on Polycarbonate containing 15% Glass Fiber. Added feature of this grade is: Impact Modified. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP WFB33E PBT (Europe-Africa-Middle East) LNP *THERMOCOMP* WFB33E is a compound based on Polybutylene Terephalate resin containing Glass Fiber and Glass Bead. Added features include Easy Molding. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ASTM D638 |
Entec Hypro™ PPC-GF40 Natural Impact Polypropylene, 40% Glass Reinforced Information provided by Entec |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO 527 |
Azoty Tarnow™ TARNOFORM 300 XEC1 POM Electrically conductive, carbon fiber reinforced injection molding grade suitable for the applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe .. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50mm/min; ISO 527 |
BASF Ultramid® 8202CQ PA6 (Dry) Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigme.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO value at 50 mm/min. |
BASF Capron® 8203C HS Blend Nylon 6 (Dry)
(discontinued **) Capron 8203C HS Blend is a heat stabilized, high viscosity nylon 6 extrusion compound possessing a modified crystalline structure for increased strength, stiffness and heat distortion temperature. .. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50 mm/min |
Arkema Group Oroglas® V 044 Acrylic, Extrusion Grade
(discontinued **) OROGLAS V 044 is an extrusion grade offering good compromise between physical properties and thermal resistance.OROGLAS V 044 is recommended for extrusion of profiles, tubes and sheets.ISO data prov.. |