Polymer Property : Tensile Modulus = 19.3 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 19.3 GPa
2800 ksi
Type I, 5.1 mm/min; ASTM D638
PolyOne LubriOne™ NL-30CF/15T Black Polyamide 612 (Nylon 612)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Modulus 19.3 GPa

@Temperature 23.9 °C
2800 ksi

@Temperature 75.0 °F
0° Direction, Dry; 325°F Autoclave; ASTM D638
Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Commercial Silica Fabric Reinforced
Nelcote® F-554 is a high purity silica filled phenolic resin coated on Commercial or Aerospace grade silica fabric. F-554 is used in the manufacture of intermediate temperature ablative rocket nozz..
Tensile Modulus 19.3 GPa
2800 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP 9X98026 PA 46 (Europe-Africa-Middle East)
LNP* Lubricomp* 9X98026 is a compound based on PA4.6 resin containing Barium Sulfate, PTFE and Carbon Fiber
Tensile Modulus 19.3 GPa
2800 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ PS-30CF/10T 2S Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced, PTFE/Silicone Lubricated
Description/Features:Carbon Fiber ReinforcedPTFE/Silicone LubricatedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Modulus 19.3 GPa
2800 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® AS-30CF/000 UV Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced  (discontinued
Description/Features:Carbon Fiber ReinforcedUV StabilizedUL 94 HB (HEM TEST)PolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Modulus 19.3 GPa
2800 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Therma-Tech™ NJ-6000C TC Nylon 12  (discontinued **)
Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of therm..
Tensile Modulus 19.3 GPa
2800 ksi
ISO 527-1/-2
Lanxess Durethan® TP 036-052 000000 Nylon 6, 60% Glass Fiber
PA 6, injection molding grade, 60% glass fibers, good flowability (Easy Flow), good heat-resistance
Tensile Modulus 19.3 GPa
2800 ksi
ASTM D638
Techmer ES Electrafil® J-3/CF/30 Nylon 6, 30% Carbon Fiber Reinforced
Tensile Modulus 19.3 GPa
2800 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON REP349 PA 66
LNP* STAT-KON* REP349 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone, 20% Carbon Fiber. Added features of this material include: Electrically Conductive, Wear Resistant.
Tensile Modulus 19.3 GPa
2800 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP VERTON UV00AS PPA (Asia Pacific)
LNP* Verton* UV00AS is a compound based on Polyphthalamide resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Modulus 19.3 GPa
2800 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP VERTON UX06451 PPA (Asia Pacific)
LNP* Verton* UX06451 is a compound based on Polyphthalamide resin containing Long Glass Fiber.
Tensile Modulus 19.3 GPa
2800 ksi
45° stress angle
Cytec Cyply® 1002 Epoxy Fiberglass Composite, Isotropic
CYPLY® 1002 is a cured epoxy composite material based on a unique non-woven parallel filament construction. This type of construction minimizes filament stress abrasion that can shorten fatigue li..
Tensile Modulus 19.3 GPa
2800 ksi
90° stress angle
Cytec Cyply® 1002 Epoxy Fiberglass Composite, Isotropic
CYPLY® 1002 is a cured epoxy composite material based on a unique non-woven parallel filament construction. This type of construction minimizes filament stress abrasion that can shorten fatigue li..
Tensile Modulus 19.3 GPa
2800 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP VERTON UV00AS PPA
LNP* VERTON* UV00AS is a compound based on Polyphthalamide resin containing 50% Long Glass Fiber. Added features of this material include: Heat Stabilized, Structural.