Polymer Property : Tensile Modulus = 2.44 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 2.44 GPa

@Thickness 6.40 mm
354 ksi

@Thickness 0.252 in
ASTM D638
SABIC Innovative Plastics Lexan® FL903 PC
Various weight reductions at 0.250"" (6.35 mm). High heat/creep resistance, excellent impact, flexural strength/rigidity. UV-stabilized.
Tensile Modulus 2.44 GPa

@Thickness 6.40 mm
354 ksi

@Thickness 0.252 in
ASTM D638
SABIC Innovative Plastics Lexan® FL900 PC (Asia Pacific)
Various weight reductions at 0.250"" (6.35 mm). High heat/creep resistance excellent impact, flexural strength/rigidity. UL94 V-1 at .157"" (3.99 mm).
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics Lexan® OQ1022 PC
Standard Flow OQ Resin
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics Lexan® OQ1022 PC (Asia Pacific)
Standard Flow OQ Resin
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics Lexan® OQ1022 PC (Europe-Africa-Middle East)
Standard Flow OQ Resin
Tensile Modulus 2.44 GPa
354 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS
LNP COLORCOMP* AX03654 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.
Tensile Modulus 2.44 GPa
354 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS (Asia Pacific)
LNP COLORCOMP* AX03654 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.
Tensile Modulus 2.44 GPa

@Thickness 6.40 mm
354 ksi

@Thickness 0.252 in
ASTM D638
SABIC Innovative Plastics Lexan® FL900 PC
Lexan* resin FL900 is a Br- & Cl-free flame retardant grade that can be foamed for weight reductions. UL-94 V1 listed at 3.9mm together with good stiffness, heat, creep and impact performance make i..
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT
LNP LUBRICOMP* WL004 is a compound based on PBT resin containing 20% PTFE. Added features of this material include: Wear Resistant.
Tensile Modulus 2.44 GPa
354 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66
Noryl GTX* GTX942 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is designed to have high melt flow for large part/thinwall injection molding. The material is designed to h..
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics NORYL LS6010 PPE+HIPS
Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for..
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Asia Pacific)
Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for..
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Europe-Africa-Middle East)
Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for..
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS
Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity...
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific)
Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity...
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Europe-Africa-Middle East)
Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity...
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics NORYL PVX0901 PPE+PS (Asia Pacific)
Multi purpose V1 grade
Tensile Modulus 2.44 GPa

@Thickness 3.20 mm
354 ksi

@Thickness 0.126 in
1mm/min; ASTM D638
LG Chemical HIPS MI750 PS, Impact Modified
Description: Injection Molding, PS, Impact Modified, High GlossApplication: Electric/Electronic Components, Stationary Articles, Food Containers, etc.CAS: 9003-55-8Information provided by LG Chemica..
Tensile Modulus 2.44 GPa
354 ksi
ASTM D638
Amco Amalloy® B9575 Polymer Alloy
Amco Amalloy B9575 is a clear performance copolymer with exceptional clarity and toughness.Very clear, high tensile and flexural strength.Information provided by Amco Plastic Materials.
Tensile Modulus 2.44 GPa

@Thickness 6.40 mm
354 ksi

@Thickness 0.252 in
ASTM D638
SABIC Innovative Plastics Lexan® FL1000 PC
5% GR. Various weight reductions at .250""(6.35mm) wall. Excellent flex strength/rigidity, high heat/creep resistance. V-0/5VA rated.