Polymer Property : Tensile Modulus = 6.30 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	6.30 GPa @Thickness 0.0500 mm	914 ksi @Thickness 0.00197 in	ASTM D882-02
NeXolve LaRC™-CP1 Conductive Black Polyimide Lower RF loss than other black and conductive black polyimides. NeXolve’s Conductive Black LaRC™-CP1 Polyimide is filled with carbon nanoparticles to produce a conductive black polyimide material ..
Tensile Modulus	6.30 GPa @Thickness 4.00 mm, Temperature 23.0 °C	914 ksi @Thickness 0.157 in, Temperature 73.4 °F	Injection Molded; ISO 527-2/1
PolyOne Bergamid™ B70 G30 BK Polyamide 6 (Nylon 6) Information provided by PolyOne
Tensile Modulus	6.30 GPa	914 ksi	Conditioned; ISO 527-1/-2
Lanxess DurethanÂ® BCF 30 X H2.0 901510 Nylon 6, 30% Glass + Carbon Fiber PA 6, injection molding grade, 30% reinforced (glass fibers + carbon fibers), conductive, intrinsic color black, good heat-ageing resistance
Tensile Modulus	6.30 GPa	914 ksi	ISO 527-1/-2
Lanxess DurethanÂ® BG 30 X H2.0 901510 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, good heat-ageing resistance
Tensile Modulus	6.30 GPa	914 ksi	ISO 527-1/-2
Lanxess DurethanÂ® BKV 15 000000 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers
Tensile Modulus	6.30 GPa	914 ksi	cond.; ISO 527-1, -2; 1 mm/min
Lanxess DurethanÂ® DP BKV 35 XF 901510 Nylon 6, 35% Glass Fiber PA 6, 35% glass fibers, injection molding, improved flowability, improved surface finishInformation provided by LANXESS.
Tensile Modulus	6.30 GPa	914 ksi
LATI Latilub 66-20T G/20 PA66, 20% Glass Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyamide 66 (PA66). PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industri..
Tensile Modulus	6.30 GPa	914 ksi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 218 V25 Black 21 N PA66, 25% glass fiber, Conditioned Description: TECHNYLÂ® A 218 V25 is a polyamide 66, reinforced with 25% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The ..
Tensile Modulus	6.30 GPa	914 ksi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 218G1 V25 Black 34N PA66, 25% glass fiber, Conditioned Description: Polyamide 66, reinforced with 25% of glass fiber, for injection molding. This grade shows an improved retention of properties after long term ageing in automotive cooling liquids. Avail..
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RX94033 PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RX94033 is a compound based on PA 66 resin containing Aramide Fiber, Glass Fiber, PTFE. Added features include: Internally Lubricated.
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® DR48 - CS1049 PBT (Europe-Africa-Middle East) VALOX DR48 is a 15 % glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromot..
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF004 PC (Europe-Africa-Middle East) LNP* THERMOCOMP* DF004 is a compound based on Polycarbonate resin containing Glass Fiber.
Tensile Modulus	6.30 GPa	914 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp DFZ42P PC LNP* Thermocomp* DFZ42P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the..
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66 LNP THERMOCOMP* RF0039S is a compound based on Nylon 66 resin containing 15% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RKN14 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RKN14 is a compound based on Nylon 66 resin containing Mineral, MOS2.
Tensile Modulus	6.30 GPa	914 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DFD03 PC LNP* STAT-KON* DFD03 is a compound based on Polycarbonate containing 15% Glass Fiber. Added feature of this grade is: Impact Modified.
Tensile Modulus	6.30 GPa	914 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® SHF4930 PBT (Europe-Africa-Middle East) Super high flow FR PBT grade with 15% Glass reinforced
Tensile Modulus	6.30 GPa	914 ksi	ISO 527-1
Sax Polymers SAXLAC 108 GF17 Acrylonitrile Butadiene Styrene, 17% Glass Fiber Saxalac 108 GF17 is a 17% glass fiber reinforced ABS injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Mechanical property data te..
Tensile Modulus	6.30 GPa	914 ksi	cond; ISO 527-1/-2
DSM Novamid® 1015GH35 BK37 PA6-GF35 35% Glass Reinforced, Heat Stabilized, Injection Molding
Tensile Modulus	6.30 GPa	914 ksi	cond; ISO 527-1/-2
DSM Novamid® 3021GH30 NAT PA66-GF30 30% Glass Reinforced, Heat Stabilized
Tensile Modulus	6.30 GPa	914 ksi	dry; ISO 527-1/-2
EMS-Grivory Grivory® EBGM-20 HX PA666-GF15 Product description: Grilon EBGM-20 HX black 9992 is a high viscosity, high heat stabilized PA66 + PA6 extrusion blow molding grade with 15% glass fibers. The special features of Grilon EBGM-20 HX b..
Tensile Modulus	6.30 GPa	914 ksi	ISO 527
CP-Polymer-Technik Wellamid® 6600 GV 25 DCHP 25% Glass Fiber Nylon 66, Special Heat Ageing Stabilization, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Modulus	6.30 GPa	914 ksi	ISO 527
CP-Polymer-Technik Wellamid® 6600 GV 25 HWCP 25% Glass Fiber Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Modulus	6.30 GPa @Temperature 120 °C	914 ksi @Temperature 248 °F	ISO 527-1/-2
DSM Stanyl® TW271B3 (PA46+PTFE)-CF15 15% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Modulus	6.30 GPa	914 ksi	1mm/min; ISO 527
BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Conditioned) Ultramid 1703-2 BK ND3007 is a 25% glass reinforced, heat stabilized injection molding nylon 6/6.
Tensile Modulus	6.30 GPa	914 ksi	same value from ASTM and ISO test.
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with..
Tensile Modulus	6.30 GPa	914 ksi	STN EN ISO 527-2
Plastcom SLOVASTER® B GB 40 PBT reinforced with glass beads PBT for injection molding, reinforced with 40% glass beads. Characterized by very good properties also at low temperature. Melt is characterized by very good rheology, which enables manufacturing of..