Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 6.96 GPa | 1010 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM AR9200 PEI 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
Tensile Modulus | 6.96 GPa | 1010 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM AR9200 PEI (Asia Pacific) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
Tensile Modulus | 6.96 GPa | 1010 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem LTX921A PEI Blend Post-industrial recycle based, 20% glass fiber filled, high flow Polyetherimide blend. ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Modulus | 6.96 GPa | 1010 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DE002ER PC LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive. |
|||
Tensile Modulus | 6.96 GPa | 1010 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DE002ER PC (Asia Pacific) LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Modulus | 6.96 GPa | 1010 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DX06411H PC LNP* THERMOCOMP* DX06411H is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare. |